Fabrication of low loss channel waveguide in tungsten-tellurite glass by 11 MeV carbon ion microbeam for telecom C band

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F19%3A00522013" target="_blank" >RIV/61389005:_____/19:00522013 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.1016/j.omx.2019.100035" target="_blank" >https://doi.org/10.1016/j.omx.2019.100035</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.omx.2019.100035" target="_blank" >10.1016/j.omx.2019.100035</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Fabrication of low loss channel waveguide in tungsten-tellurite glass by 11 MeV carbon ion microbeam for telecom C band

Popis výsledku v původním jazyce

Channel waveguides were directly written in Er: TeO2W2O3 glass using 11 MeV C4+ ion microbeam with fluences in the range of 1·1014–5·1016 ion/cm2. The channel waveguides supported a single guided mode at Lambda = 1540 nm. Propagation losses of the as-irradiated channel waveguides were around 14 dB/cm. A 30-min thermal annealing at 150 °C in air reduced propagation losses at Lambda = 1400 nm to 1.5 dB/cm. This method produced channel waveguides with confinement and propagation losses comparable to or better than other current methods, such as MeV energy focused proton or helium ion beam writing.

Název v anglickém jazyce

Fabrication of low loss channel waveguide in tungsten-tellurite glass by 11 MeV carbon ion microbeam for telecom C band

Popis výsledku anglicky

Channel waveguides were directly written in Er: TeO2W2O3 glass using 11 MeV C4+ ion microbeam with fluences in the range of 1·1014–5·1016 ion/cm2. The channel waveguides supported a single guided mode at Lambda = 1540 nm. Propagation losses of the as-irradiated channel waveguides were around 14 dB/cm. A 30-min thermal annealing at 150 °C in air reduced propagation losses at Lambda = 1400 nm to 1.5 dB/cm. This method produced channel waveguides with confinement and propagation losses comparable to or better than other current methods, such as MeV energy focused proton or helium ion beam writing.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

10304 - Nuclear physics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Optical Materials: X

ISSN

2590-1478

e-ISSN

—

Svazek periodika

4

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

100035

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85072950051