Effect of temperature on fatigue of superelastic NiTi wires

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F20%3A00523756" target="_blank" >RIV/61389005:_____/20:00523756 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/20:00525010 RIV/68407700:21340/20:00344886 RIV/00216305:26620/20:PU140210

Výsledek na webu

<a href="https://doi.org/10.1016/j.ijfatigue.2020.105470" target="_blank" >https://doi.org/10.1016/j.ijfatigue.2020.105470</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ijfatigue.2020.105470" target="_blank" >10.1016/j.ijfatigue.2020.105470</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of temperature on fatigue of superelastic NiTi wires

Popis výsledku v původním jazyce

The stress induced martensitic transformation in superelastic NiTi alloy can be accompanied by a plastic deformation. In this work, NiTi wires were subjected to tensile displacement-controlled tests in the temperature range -90 degrees C to 190 degrees C and lattice defects created by the deformation were analysed by TEM. The unrecovered strain significantly increased and fatigue life decreased with increasing test temperature. The rate of the accumulation of unrecovered strain in the stabilized stage of tensile cycling was taken as an indicator of the accumulation of material damage. Fatigue life ranged from 900 cycles at 80 degrees C to 4700 cycles at 15 degrees C.

Název v anglickém jazyce

Effect of temperature on fatigue of superelastic NiTi wires

Popis výsledku anglicky

The stress induced martensitic transformation in superelastic NiTi alloy can be accompanied by a plastic deformation. In this work, NiTi wires were subjected to tensile displacement-controlled tests in the temperature range -90 degrees C to 190 degrees C and lattice defects created by the deformation were analysed by TEM. The unrecovered strain significantly increased and fatigue life decreased with increasing test temperature. The rate of the accumulation of unrecovered strain in the stabilized stage of tensile cycling was taken as an indicator of the accumulation of material damage. Fatigue life ranged from 900 cycles at 80 degrees C to 4700 cycles at 15 degrees C.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International Journal of Fatigue

ISSN

0142-1123

e-ISSN

—

Svazek periodika

134

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

105470

Kód UT WoS článku

000518708500008

EID výsledku v databázi Scopus

2-s2.0-85077738883