Residual Stress Measurements in the Vicinity of the Butt Weld on the Spherical Storage Tank

Popis výsledku v původním jazyce

The identification of the residual stress distribution is an important part of the analysis for the evaluation of life time of steel structures and for an estimation of their critical defect size. Stresses bring about local deformation in weld area and influence properties and behaviour of these structures during service. In this paper the results of strain/stress measurements in the vicinity of the butt weld on the spherical storage tank by neutron diffraction are presented. The storage tank was made of C-Mn unalloyed steel of the strength of ≈ 430 MPa. The specimen in the form of a plate with the dimensions of 100x145x15 mm3 (width x length x thickness). The measurements revealed maximum residual stresses on the level of 300 MPa, 150 MPa and 200 MPa in the longitudinal, transversal and normal direction, respectively.

Název v anglickém jazyce

Residual Stress Measurements in the Vicinity of the Butt Weld on the Spherical Storage Tank

Popis výsledku anglicky

The identification of the residual stress distribution is an important part of the analysis for the evaluation of life time of steel structures and for an estimation of their critical defect size. Stresses bring about local deformation in weld area and influence properties and behaviour of these structures during service. In this paper the results of strain/stress measurements in the vicinity of the butt weld on the spherical storage tank by neutron diffraction are presented. The storage tank was made of C-Mn unalloyed steel of the strength of ≈ 430 MPa. The specimen in the form of a plate with the dimensions of 100x145x15 mm3 (width x length x thickness). The measurements revealed maximum residual stresses on the level of 300 MPa, 150 MPa and 200 MPa in the longitudinal, transversal and normal direction, respectively.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

The Proceedings of the European Research Reactor Conference

ISBN

978-92-95064-36-2

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

European Nuclear Society

Místo vydání

Brusel

Místo konání akce

Helsinki

Datum konání akce

24. 9. 2021

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—