The effect of a polypyrrole coating on the thermal stability of microporous polyethylene membranes.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F03%3A55033008" target="_blank" >RIV/61389013:_____/03:55033008 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of a polypyrrole coating on the thermal stability of microporous polyethylene membranes.

Popis výsledku v původním jazyce

Microporous polyethylene (PE) membranes were coated on both sides with a polypyrrole (PPy) overlayer. PPy was deposited also on the walls of pores. Thermodeformation measurements indicate that the hard framework produced by rigid-chain PPy controls the mechanical properties of composite membranes. FTIR spectroscopy was used to detect oxidative processes in both polymer components above 200 C. Elemental analysis showed that the nitrogen content remains at high level, even after the treatment of membranesin air at 300 C, indicating that the decomposition involved mainly PE while PPy was much more stable.

Název v anglickém jazyce

The effect of a polypyrrole coating on the thermal stability of microporous polyethylene membranes.

Popis výsledku anglicky

Microporous polyethylene (PE) membranes were coated on both sides with a polypyrrole (PPy) overlayer. PPy was deposited also on the walls of pores. Thermodeformation measurements indicate that the hard framework produced by rigid-chain PPy controls the mechanical properties of composite membranes. FTIR spectroscopy was used to detect oxidative processes in both polymer components above 200 C. Elemental analysis showed that the nitrogen content remains at high level, even after the treatment of membranesin air at 300 C, indicating that the decomposition involved mainly PE while PPy was much more stable.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

European Polymer Journal

ISSN

0014-3057

e-ISSN

—

Svazek periodika

39

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

8

Strana od-do

647-654

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—