Nucleation of isotactic polypropylene crystallization by gold nanoparticles
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F10%3A00338149" target="_blank" >RIV/61389013:_____/10:00338149 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Nucleation of isotactic polypropylene crystallization by gold nanoparticles
Popis výsledku v původním jazyce
Nucleation of isotactic polypropylene (iPP) crystallization by gold (Au) nanoparticles was studied. Regardless of their size, 4.3, 8.8, 28.3, and 84.5 nm, all particles were able to nucleate spherulites when deposited on the iPP surface. However, when added and melt-mixed with iPP, only the smallest particles affected significantly the iPP bulk crystallization. Au nanoparticles larger than 4.3 nm, at the concentration of 0.001 wt %, did not influence the crystallization of iPP. Contrary to this, 0.001 and 0.005 wt % of Au nanoparticles having the size of 4.3 nm increased crystallization temperature of the iPP by 7-8 °C and decreased markedly the sizes of polycrystalline aggregates. Aggregation of Au nanoparticles in the polymer matrix was evidenced byelectron microscopy and contributed to their decreased effectiveness in the nucleation of iPP crystallization.
Název v anglickém jazyce
Nucleation of isotactic polypropylene crystallization by gold nanoparticles
Popis výsledku anglicky
Nucleation of isotactic polypropylene (iPP) crystallization by gold (Au) nanoparticles was studied. Regardless of their size, 4.3, 8.8, 28.3, and 84.5 nm, all particles were able to nucleate spherulites when deposited on the iPP surface. However, when added and melt-mixed with iPP, only the smallest particles affected significantly the iPP bulk crystallization. Au nanoparticles larger than 4.3 nm, at the concentration of 0.001 wt %, did not influence the crystallization of iPP. Contrary to this, 0.001 and 0.005 wt % of Au nanoparticles having the size of 4.3 nm increased crystallization temperature of the iPP by 7-8 °C and decreased markedly the sizes of polycrystalline aggregates. Aggregation of Au nanoparticles in the polymer matrix was evidenced byelectron microscopy and contributed to their decreased effectiveness in the nucleation of iPP crystallization.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/KAN200520704" target="_blank" >KAN200520704: Nové nanopartikule pro ultrastrukturální diagnostiku</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Polymer Science. Polymer Physics Edition
ISSN
0887-6266
e-ISSN
—
Svazek periodika
48
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
10
Strana od-do
—
Kód UT WoS článku
000274751200010
EID výsledku v databázi Scopus
—