Synthesis and characterization of calix[4]arene-containing polyimides

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F11%3A00356497" target="_blank" >RIV/61389013:_____/11:00356497 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/11:43892356

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Synthesis and characterization of calix[4]arene-containing polyimides

Popis výsledku v původním jazyce

Three types of amino-functionalized calixarenes, i.e. the diaminocalix[4]arenes 5,17-diaminomethyl-25,26,27,28-tetrapropoxycalix[4]arene, 25,27-diaminoethoxy-26,28-dihydroxycalix[4]arene and 5,11,17,23-tetra-tert-butyl-25,27-diaminoethoxy-26,28-dihydroxycalix[4]arene, were synthesized and incorporated as comonomers into the backbones of polyimides. As a first step, (poly(amic acid)s) were prepared by condensation reaction of diamine with dianhydride at the stoichiometric ratio. The diamine component wascomposed of synthesized diaminocalix[4]arene and commercial 4,4-oxydianiline combined in various molar ratios. The dianhydride used was 4,4-oxydiphthalic anhydride. The poly(amic acid)s were characterized by viscosity and 1H NMR spectroscopy. The precursors were then transformed into the polyimides using a thermal treatment. Thermal and dynamic mechanical behaviour, wide-angle X-ray diffraction and solubility of the resulting polyimide films in selected solvents were evaluated.

Název v anglickém jazyce

Synthesis and characterization of calix[4]arene-containing polyimides

Popis výsledku anglicky

Three types of amino-functionalized calixarenes, i.e. the diaminocalix[4]arenes 5,17-diaminomethyl-25,26,27,28-tetrapropoxycalix[4]arene, 25,27-diaminoethoxy-26,28-dihydroxycalix[4]arene and 5,11,17,23-tetra-tert-butyl-25,27-diaminoethoxy-26,28-dihydroxycalix[4]arene, were synthesized and incorporated as comonomers into the backbones of polyimides. As a first step, (poly(amic acid)s) were prepared by condensation reaction of diamine with dianhydride at the stoichiometric ratio. The diamine component wascomposed of synthesized diaminocalix[4]arene and commercial 4,4-oxydianiline combined in various molar ratios. The dianhydride used was 4,4-oxydiphthalic anhydride. The poly(amic acid)s were characterized by viscosity and 1H NMR spectroscopy. The precursors were then transformed into the polyimides using a thermal treatment. Thermal and dynamic mechanical behaviour, wide-angle X-ray diffraction and solubility of the resulting polyimide films in selected solvents were evaluated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CD - Makromolekulární chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA104%2F09%2F1357" target="_blank" >GA104/09/1357: Příprava a vlastnosti kombinovaných materiálů vysoce větvený polyimid - oxid křemičitý využitelných jako separační membrány</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Polymer International

ISSN

0959-8103

e-ISSN

—

Svazek periodika

60

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

000288133700009

EID výsledku v databázi Scopus

—