Processing-improved properties and morphology of PP/COC blends
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F11%3A00362902" target="_blank" >RIV/61389013:_____/11:00362902 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1002/app.34258" target="_blank" >http://dx.doi.org/10.1002/app.34258</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/app.34258" target="_blank" >10.1002/app.34258</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Processing-improved properties and morphology of PP/COC blends
Popis výsledku v původním jazyce
The aim of this study was to improve mechanical properties of polypropylene/cycloolefin copolymer (PP/COC) blends by processing-induced formation of long COC fibers. We focused our attention on finding processing conditions yielding PP/COC fibrous morphology in a well-defined, reproducible way. A number of PP/COC blends were prepared by both compression molding and injection molding (IM). Neat polymers were characterized by rheological measurements, whereas phase morphology of the resulting blends was characterized by means of scanning electron microscopy. The longest COC fibers were achieved in the injection molded PP/COC blends with compositions 75/25 and 70/30 wt %. Elastic modulus and yield strength were measured as functions of the blend composition using an Instron tensile tester; statistically significant improvement of the yield strength due to fibrous morphology was proved.
Název v anglickém jazyce
Processing-improved properties and morphology of PP/COC blends
Popis výsledku anglicky
The aim of this study was to improve mechanical properties of polypropylene/cycloolefin copolymer (PP/COC) blends by processing-induced formation of long COC fibers. We focused our attention on finding processing conditions yielding PP/COC fibrous morphology in a well-defined, reproducible way. A number of PP/COC blends were prepared by both compression molding and injection molding (IM). Neat polymers were characterized by rheological measurements, whereas phase morphology of the resulting blends was characterized by means of scanning electron microscopy. The longest COC fibers were achieved in the injection molded PP/COC blends with compositions 75/25 and 70/30 wt %. Elastic modulus and yield strength were measured as functions of the blend composition using an Instron tensile tester; statistically significant improvement of the yield strength due to fibrous morphology was proved.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP106%2F09%2FP272" target="_blank" >GP106/09/P272: Zvyšování rozměrové stability polymerních směsí s vyváženými mechanickými vlastnostmi</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Applied Polymer Science
ISSN
0021-8995
e-ISSN
—
Svazek periodika
122
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
8
Strana od-do
1168-1175
Kód UT WoS článku
000293741800053
EID výsledku v databázi Scopus
—