HDPE/COC blends with fibrous morphology and their properties
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F12%3A00382273" target="_blank" >RIV/61389013:_____/12:00382273 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.eurpolymj.2012.09.005" target="_blank" >http://dx.doi.org/10.1016/j.eurpolymj.2012.09.005</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.eurpolymj.2012.09.005" target="_blank" >10.1016/j.eurpolymj.2012.09.005</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
HDPE/COC blends with fibrous morphology and their properties
Popis výsledku v původním jazyce
High-density polyethylene/cycloolefin copolymer (HDPE/COC) blends were prepared using an optimized process resulting in fibrous morphology of COC. Based on rheological data and theoretical predictions, the research was focused on three HDPE?s with high viscosity and on the HDPE/COC compositions with 20, 30 and 40 wt.% of COC. A significant increase in both macromechanical and micromechanical properties of softer HDPE matrix due to tougher oriented COC fibres was achieved in all cases. Combined results from scanning electron microscopy, tensile testing, microhardness measurements and theoretical calculations based on Equivalent Box Model (EBM) showed that the interfacial adhesion is unusually high and indicated partial miscibility of the components.
Název v anglickém jazyce
HDPE/COC blends with fibrous morphology and their properties
Popis výsledku anglicky
High-density polyethylene/cycloolefin copolymer (HDPE/COC) blends were prepared using an optimized process resulting in fibrous morphology of COC. Based on rheological data and theoretical predictions, the research was focused on three HDPE?s with high viscosity and on the HDPE/COC compositions with 20, 30 and 40 wt.% of COC. A significant increase in both macromechanical and micromechanical properties of softer HDPE matrix due to tougher oriented COC fibres was achieved in all cases. Combined results from scanning electron microscopy, tensile testing, microhardness measurements and theoretical calculations based on Equivalent Box Model (EBM) showed that the interfacial adhesion is unusually high and indicated partial miscibility of the components.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GP106%2F09%2FP272" target="_blank" >GP106/09/P272: Zvyšování rozměrové stability polymerních směsí s vyváženými mechanickými vlastnostmi</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
European Polymer Journal
ISSN
0014-3057
e-ISSN
—
Svazek periodika
48
Číslo periodika v rámci svazku
12
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
9
Strana od-do
2031-2039
Kód UT WoS článku
000311600400007
EID výsledku v databázi Scopus
—