Conducting polyaniline/multi-wall carbon nanotubes composite paints on low carbon steel for corrosion protection: electrochemical investigations
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F13%3A00392177" target="_blank" >RIV/61389013:_____/13:00392177 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.2478/s11696-012-0273-9" target="_blank" >http://dx.doi.org/10.2478/s11696-012-0273-9</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.2478/s11696-012-0273-9" target="_blank" >10.2478/s11696-012-0273-9</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Conducting polyaniline/multi-wall carbon nanotubes composite paints on low carbon steel for corrosion protection: electrochemical investigations
Popis výsledku v původním jazyce
The coaxial coating of multi-wall carbon nanotubes (MWCNT) with poly(aniline) (PANI) was synthesised and a paint was prepared containing conducting PANI-MWCNT composite. The corrosion protection performance was assessed by open circuit potential measurements, potentiodynamic polarisation, and electrochemical impedance spectroscopy. The corrosion rate of low-carbon steel coated with 1.5 mass % of PANI-MWCNT-based paint in 3.5 mass % sodium chloride solution was found to be 0.037 mm y1, about 5.2 times lower than that of unpainted low-carbon steel and 3.6 times lower than that of epoxy painted steel.
Název v anglickém jazyce
Conducting polyaniline/multi-wall carbon nanotubes composite paints on low carbon steel for corrosion protection: electrochemical investigations
Popis výsledku anglicky
The coaxial coating of multi-wall carbon nanotubes (MWCNT) with poly(aniline) (PANI) was synthesised and a paint was prepared containing conducting PANI-MWCNT composite. The corrosion protection performance was assessed by open circuit potential measurements, potentiodynamic polarisation, and electrochemical impedance spectroscopy. The corrosion rate of low-carbon steel coated with 1.5 mass % of PANI-MWCNT-based paint in 3.5 mass % sodium chloride solution was found to be 0.037 mm y1, about 5.2 times lower than that of unpainted low-carbon steel and 3.6 times lower than that of epoxy painted steel.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JI - Kompositní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F09%2F1626" target="_blank" >GA202/09/1626: Inteligentní kapaliny a komposity s řízenou strukturou</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Chemical Papers
ISSN
0366-6352
e-ISSN
—
Svazek periodika
67
Číslo periodika v rámci svazku
8
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
7
Strana od-do
1072-1078
Kód UT WoS článku
000318443700025
EID výsledku v databázi Scopus
—