Influence of pyrolysis temperature on fracture response in SiOC based composites reinforced by basalt woven fabric
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F14%3A00433976" target="_blank" >RIV/61389013:_____/14:00433976 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68081723:_____/14:00433976 RIV/67985891:_____/14:00433976 RIV/00216305:26210/14:PU110219
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2014.03.003" target="_blank" >http://dx.doi.org/10.1016/j.jeurceramsoc.2014.03.003</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2014.03.003" target="_blank" >10.1016/j.jeurceramsoc.2014.03.003</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of pyrolysis temperature on fracture response in SiOC based composites reinforced by basalt woven fabric
Popis výsledku v původním jazyce
The fracture resistance of ceramic based composites reinforced by various ceramic fibres can be dramatically enhanced when an efficient fracture mechanism takes place during the crack propagation. Presented work shows an effect of the pyrolysis temperature of the composite matrix on the fracture behaviour of the composite. The matrix is formed from the polysiloxane resin precursor and the reinforcement is a basalt woven fabric. The temperature range under investigation was from 600°C, where the onset offracture properties were observed up to 800°C. Above this temperature basalt fibres suffer by rapid degradation of the microstructure. The optimum stage of the polysiloxane resin transformation maximizing the fracture resistance of the composite was identified. The fractographic analysis of the fracture surfaces revealed the differences in the acting fracture mechanism.
Název v anglickém jazyce
Influence of pyrolysis temperature on fracture response in SiOC based composites reinforced by basalt woven fabric
Popis výsledku anglicky
The fracture resistance of ceramic based composites reinforced by various ceramic fibres can be dramatically enhanced when an efficient fracture mechanism takes place during the crack propagation. Presented work shows an effect of the pyrolysis temperature of the composite matrix on the fracture behaviour of the composite. The matrix is formed from the polysiloxane resin precursor and the reinforcement is a basalt woven fabric. The temperature range under investigation was from 600°C, where the onset offracture properties were observed up to 800°C. Above this temperature basalt fibres suffer by rapid degradation of the microstructure. The optimum stage of the polysiloxane resin transformation maximizing the fracture resistance of the composite was identified. The fractographic analysis of the fracture surfaces revealed the differences in the acting fracture mechanism.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JH - Keramika, žáruvzdorné materiály a skla
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the European Ceramic Society
ISSN
0955-2219
e-ISSN
—
Svazek periodika
34
Číslo periodika v rámci svazku
14
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
10
Strana od-do
3389-3398
Kód UT WoS článku
000340222800018
EID výsledku v databázi Scopus
—