Polyaniline/polybenzimidazole blends: characterisation of its physico-chemical properties and gas separation behaviour
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F16%3A00458013" target="_blank" >RIV/61389013:_____/16:00458013 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11310/16:10332101
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.eurpolymj.2016.02.008" target="_blank" >http://dx.doi.org/10.1016/j.eurpolymj.2016.02.008</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.eurpolymj.2016.02.008" target="_blank" >10.1016/j.eurpolymj.2016.02.008</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Polyaniline/polybenzimidazole blends: characterisation of its physico-chemical properties and gas separation behaviour
Popis výsledku v původním jazyce
Novel polymer blends were prepared by casting blend solutions of polyaniline (PANI) and polybenzimidazole (PBI) at various ratios. Prepared blends were amorphous and had good film homogeneity without defects. From mechanical analysis it was found that tensile strength diminishes with increasing content of PANI. WAXS analysis disclosed the amorphous structure of PANI/PBI blends. IR spectra indicate clearly the presence of PANI in PBI matrix and NMR spectra revealed significant interactions of PBI with PANI. Permeability, diffusion, solubility coefficients and sorption capacities of all measured gases (H2, O2, CH4, N2, CO2 and water vapour) decreased with increasing PANI content whereas ideal selectivities increased for all observed gas pairs. Doping of blends with hydrochloric acid led to a significant decrease in permeabilities and sorption capacities while selectivities slightly increased.
Název v anglickém jazyce
Polyaniline/polybenzimidazole blends: characterisation of its physico-chemical properties and gas separation behaviour
Popis výsledku anglicky
Novel polymer blends were prepared by casting blend solutions of polyaniline (PANI) and polybenzimidazole (PBI) at various ratios. Prepared blends were amorphous and had good film homogeneity without defects. From mechanical analysis it was found that tensile strength diminishes with increasing content of PANI. WAXS analysis disclosed the amorphous structure of PANI/PBI blends. IR spectra indicate clearly the presence of PANI in PBI matrix and NMR spectra revealed significant interactions of PBI with PANI. Permeability, diffusion, solubility coefficients and sorption capacities of all measured gases (H2, O2, CH4, N2, CO2 and water vapour) decreased with increasing PANI content whereas ideal selectivities increased for all observed gas pairs. Doping of blends with hydrochloric acid led to a significant decrease in permeabilities and sorption capacities while selectivities slightly increased.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GPP106%2F12%2FP643" target="_blank" >GPP106/12/P643: Příprava a charakterizace nových typů kompozitních materiálů pro membránové separace plynů</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
European Polymer Journal
ISSN
0014-3057
e-ISSN
—
Svazek periodika
77
Číslo periodika v rámci svazku
April
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
16
Strana od-do
98-113
Kód UT WoS článku
000373657900009
EID výsledku v databázi Scopus
2-s2.0-84960341450