Reduction of silver ions to silver with polyaniline/poly(vinyl alcohol) cryogels and aerogels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F18%3A00490816" target="_blank" >RIV/61389013:_____/18:00490816 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/18:10439666

Výsledek na webu

<a href="http://dx.doi.org/10.1007/s11696-017-0374-6" target="_blank" >http://dx.doi.org/10.1007/s11696-017-0374-6</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1007/s11696-017-0374-6" target="_blank" >10.1007/s11696-017-0374-6</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Reduction of silver ions to silver with polyaniline/poly(vinyl alcohol) cryogels and aerogels

Popis výsledku v původním jazyce

The macroporous conducting polymer cryogels were prepared by the oxidation of aniline hydrochloride in the frozen aqueous solutions of poly(vinyl alcohol) at − 24 °C. Corresponding polyaniline aerogels supported with poly(vinyl alcohol) have been obtained after thawing of cryogels followed by freeze-drying. Silver was deposited on the composites using the ability of polyaniline to reduce silver ions after the immersion in silver nitrate solutions. Swollen cryogels were coated only on the surface with macroscopic silver particles due to the closed-pore structure in cryogels and limited penetration of silver ions into macropores. The diffusion of silver ions to freeze-dried aerogels was better and further improved by vacuum treatment. Silver microcubes were produced in the pores, the weight fraction of silver in dry composites being typically several per cent, a maximum 13 wt%. The conductivity of the aerogels compressed to pellets depended on the processing and the highest value was 0.27 S cm−1. The aerogels containing silver were characterized in detail with Raman spectroscopy.

Název v anglickém jazyce

Reduction of silver ions to silver with polyaniline/poly(vinyl alcohol) cryogels and aerogels

Popis výsledku anglicky

The macroporous conducting polymer cryogels were prepared by the oxidation of aniline hydrochloride in the frozen aqueous solutions of poly(vinyl alcohol) at − 24 °C. Corresponding polyaniline aerogels supported with poly(vinyl alcohol) have been obtained after thawing of cryogels followed by freeze-drying. Silver was deposited on the composites using the ability of polyaniline to reduce silver ions after the immersion in silver nitrate solutions. Swollen cryogels were coated only on the surface with macroscopic silver particles due to the closed-pore structure in cryogels and limited penetration of silver ions into macropores. The diffusion of silver ions to freeze-dried aerogels was better and further improved by vacuum treatment. Silver microcubes were produced in the pores, the weight fraction of silver in dry composites being typically several per cent, a maximum 13 wt%. The conductivity of the aerogels compressed to pellets depended on the processing and the highest value was 0.27 S cm−1. The aerogels containing silver were characterized in detail with Raman spectroscopy.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10404 - Polymer science

Projekt

<a href="/cs/project/GA16-02787S" target="_blank" >GA16-02787S: Vodivé polymerní kryogely</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Chemical Papers

ISSN

0366-6352

e-ISSN

—

Svazek periodika

72

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

10

Strana od-do

1619-1628

Kód UT WoS článku

000435829800005

EID výsledku v databázi Scopus

2-s2.0-85048809572