Newly developed gel polymer electrolytes based on crosslinked poly(2-oxazolines)

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F23%3A00565342" target="_blank" >RIV/61389013:_____/23:00565342 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26220/22:PU146584 RIV/00216208:11310/23:10466913

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0167273822002454?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0167273822002454?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.ssi.2022.116096" target="_blank" >10.1016/j.ssi.2022.116096</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Newly developed gel polymer electrolytes based on crosslinked poly(2-oxazolines)

Popis výsledku v původním jazyce

Advanced materials based on polyoxazoline chemistry are presented as electrochemically, mechanically and thermally stable, efficient and versatile “green” gel polymer electrolytes (GPEs). A series of GPEs was prepared by cationic ring-opening copolymerization (CROP) of two 2-oxazolines with different ratios of the comonomers and their subsequent crosslinking and swelling in Li salt solution. The samples were investigated in terms of their ionic conductivity, thermal properties and ionic diffusion. Finally, a lithium stripping/plating experiment was used to evaluate their electrochemical stability. Promising electrolytes possessing high conductivity (3.7·10−4 S/cm at 20 °C) and excellent durability were obtained.

Název v anglickém jazyce

Newly developed gel polymer electrolytes based on crosslinked poly(2-oxazolines)

Popis výsledku anglicky

Advanced materials based on polyoxazoline chemistry are presented as electrochemically, mechanically and thermally stable, efficient and versatile “green” gel polymer electrolytes (GPEs). A series of GPEs was prepared by cationic ring-opening copolymerization (CROP) of two 2-oxazolines with different ratios of the comonomers and their subsequent crosslinking and swelling in Li salt solution. The samples were investigated in terms of their ionic conductivity, thermal properties and ionic diffusion. Finally, a lithium stripping/plating experiment was used to evaluate their electrochemical stability. Promising electrolytes possessing high conductivity (3.7·10−4 S/cm at 20 °C) and excellent durability were obtained.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10404 - Polymer science

Projekt

<a href="/cs/project/GA20-01233S" target="_blank" >GA20-01233S: Racionální design pokročilých měkkých funkčních materiálů řízený pokročilou NMR spektroskopií pevného stavu a vysoce výkonnou elektronovou mikroskopií</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Solid State Ionics

ISSN

0167-2738

e-ISSN

1872-7689

Svazek periodika

389

Číslo periodika v rámci svazku

January

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

10

Strana od-do

116096

Kód UT WoS článku

000961043600003

EID výsledku v databázi Scopus

2-s2.0-85145602901