Eroze jehlových elektrod v impulsním korónovém výboji ve vodě

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F06%3A00042399" target="_blank" >RIV/61389021:_____/06:00042399 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Erosion of needle electrodes in pulsed corona discharge in water

Popis výsledku v původním jazyce

Erosion of needle electrodes in the pulsed corona discharge in water with a pulse energy of 2-3 J was investigated in dependence on the electrode material (platinum, tungsten and stainless-steel) and the solution conductivity (100 and 500 ?S/cm). Erosionof electrodes remarkable increased with the higher solution conductivity for all three tested metals. The highest erosion rates were determined for tungsten while platinum was the least eroded material. In addition to the dominant melting effect, release of anode material by the electrolysis significantly contributed to the total erosion of needle electrodes. The highest contribution of electrolysis was determined for stainless-steel electrodes that released up to 40-50% of eroded metal in the form ofiron ions. Peculiar protrusions were observed on the surface of eroded tungsten electrodes.

Název v anglickém jazyce

Erosion of needle electrodes in pulsed corona discharge in water

Popis výsledku anglicky

Erosion of needle electrodes in the pulsed corona discharge in water with a pulse energy of 2-3 J was investigated in dependence on the electrode material (platinum, tungsten and stainless-steel) and the solution conductivity (100 and 500 ?S/cm). Erosionof electrodes remarkable increased with the higher solution conductivity for all three tested metals. The highest erosion rates were determined for tungsten while platinum was the least eroded material. In addition to the dominant melting effect, release of anode material by the electrolysis significantly contributed to the total erosion of needle electrodes. The highest contribution of electrolysis was determined for stainless-steel electrodes that released up to 40-50% of eroded metal in the form ofiron ions. Peculiar protrusions were observed on the surface of eroded tungsten electrodes.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

<a href="/cs/project/KSK2043105" target="_blank" >KSK2043105: Procesy v plazmatu a interakce záření s hmotou</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Czechoslovak Journal of Physics

ISSN

0011-4626

e-ISSN

—

Svazek periodika

56

Číslo periodika v rámci svazku

suppl. B

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

18

Strana od-do

916-924

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—