Plasma Spraying and Characterization of Tungsten Carbide-Cobalt Coatings by the Water-Stabilized System WSP

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F09%3A00341118" target="_blank" >RIV/61389021:_____/09:00341118 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Plasma Spraying and Characterization of Tungsten Carbide-Cobalt Coatings by the Water-Stabilized System WSP

Popis výsledku v původním jazyce

Tungsten carbide-cobalt powders (WC-17wt% Co) were plasma sprayed by a water-stabilized system WSP. Experiments with variable feeding distances and spray distances were carried out. Thinner coatings were deposited on carbon steel substrates and thicker coatings on stainless steel substrates to compare different cooling conditions. Basic characterization of coatings was done by XRD, SEM, and light microscopy plus image analysis.Microhardness was measured on polished cross-sections. The main focus of investigation was resistance against wear in dry as well as wet conditions. The appropriate tests were performed with set-ups based on ASTM G65 and G75, respectively. The influence of spray parameters onto coating wear performance was observed. The results of mechanical tests were discussed in connection with changes of phase composition and with the quality of the coating's microstructure.

Název v anglickém jazyce

Plasma Spraying and Characterization of Tungsten Carbide-Cobalt Coatings by the Water-Stabilized System WSP

Popis výsledku anglicky

Tungsten carbide-cobalt powders (WC-17wt% Co) were plasma sprayed by a water-stabilized system WSP. Experiments with variable feeding distances and spray distances were carried out. Thinner coatings were deposited on carbon steel substrates and thicker coatings on stainless steel substrates to compare different cooling conditions. Basic characterization of coatings was done by XRD, SEM, and light microscopy plus image analysis.Microhardness was measured on polished cross-sections. The main focus of investigation was resistance against wear in dry as well as wet conditions. The appropriate tests were performed with set-ups based on ASTM G65 and G75, respectively. The influence of spray parameters onto coating wear performance was observed. The results of mechanical tests were discussed in connection with changes of phase composition and with the quality of the coating's microstructure.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/1QS200430560" target="_blank" >1QS200430560: Progresivní žárové nástřiky odolné proti otěru</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Advances in Materials Science and Engineering

ISSN

1687-8434

e-ISSN

—

Svazek periodika

2009

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—