Powder metallurgy preparation of Al-Cu-Fe quasicrystals using mechanical alloying and Spark Plasma Sintering

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F14%3A00428488" target="_blank" >RIV/61389021:_____/14:00428488 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60461373:22310/14:43898096

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S0966979514001198#" target="_blank" >http://www.sciencedirect.com/science/article/pii/S0966979514001198#</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.intermet.2014.04.003" target="_blank" >10.1016/j.intermet.2014.04.003</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Powder metallurgy preparation of Al-Cu-Fe quasicrystals using mechanical alloying and Spark Plasma Sintering

Popis výsledku v původním jazyce

This work is devoted to the preparation of ultrafine material based on AleCueFe quasicrystalline phase by powder metallurgy using mechanical alloying and Spark Plasma Sintering. The dependence of microstructure and phase composition of powders on the conditions of mechanical alloying was described. It was found that the Al60Cu30Fe10 quasicrystalline phase forms directly already after 2 h of milling under optimized conditions. The stability of this quasicrystalline phase was studied at various temperatures of Spark Plasma Sintering compaction process.

Název v anglickém jazyce

Powder metallurgy preparation of Al-Cu-Fe quasicrystals using mechanical alloying and Spark Plasma Sintering

Popis výsledku anglicky

This work is devoted to the preparation of ultrafine material based on AleCueFe quasicrystalline phase by powder metallurgy using mechanical alloying and Spark Plasma Sintering. The dependence of microstructure and phase composition of powders on the conditions of mechanical alloying was described. It was found that the Al60Cu30Fe10 quasicrystalline phase forms directly already after 2 h of milling under optimized conditions. The stability of this quasicrystalline phase was studied at various temperatures of Spark Plasma Sintering compaction process.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GBP108%2F12%2FG043" target="_blank" >GBP108/12/G043: Mikro- a nanokrystalické materiály s vysokým podílem rozhraní pro moderní strukturní aplikace, biodegradabilní implantáty a uchovávání vodíku</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Intermetallics

ISSN

0966-9795

e-ISSN

—

Svazek periodika

52

Číslo periodika v rámci svazku

September

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

7

Strana od-do

131-137

Kód UT WoS článku

000336873700018

EID výsledku v databázi Scopus

—