Boronized stainless steel with zirconia coatings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F15%3A00456147" target="_blank" >RIV/61389021:_____/15:00456147 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Boronized stainless steel with zirconia coatings

Popis výsledku v původním jazyce

Conditions of boronizing are described using a reactive diffusion method of boron from boron carbide and lanthanum hexaboride so that the formation of Fe2B is preferred to FeB which is more brittle and whose structure does not satisfy the conditions forperfect adhesion of modified zirconia ceramics. Perfectly rigid adhesive connection of needle-like embedded interlayers Fe2B in steel AISI 303 prepared by reactive diffusion of a boronizing medium without activators at 1000 ° C and exposure of 2-4 hourshas the value of 20 - 24 MPa at the Pinn-off test.Ceramic coatings from Al2O3-ZrO2 ceramics formed on those interlayers have the value of bond strength up to 14 - 20 MPa.Thermal cycling between 100°C - 600 °C confirmed good adhesion of coatings with theunderlying steel.During thermal cycling at elevated temperatures (600-1000 °C) there occurs a statistically significant number of faults in cohesion and mechanical destruction of the coatings. One of the reasons are secondary changes

Název v anglickém jazyce

Boronized stainless steel with zirconia coatings

Popis výsledku anglicky

Conditions of boronizing are described using a reactive diffusion method of boron from boron carbide and lanthanum hexaboride so that the formation of Fe2B is preferred to FeB which is more brittle and whose structure does not satisfy the conditions forperfect adhesion of modified zirconia ceramics. Perfectly rigid adhesive connection of needle-like embedded interlayers Fe2B in steel AISI 303 prepared by reactive diffusion of a boronizing medium without activators at 1000 ° C and exposure of 2-4 hourshas the value of 20 - 24 MPa at the Pinn-off test.Ceramic coatings from Al2O3-ZrO2 ceramics formed on those interlayers have the value of bond strength up to 14 - 20 MPa.Thermal cycling between 100°C - 600 °C confirmed good adhesion of coatings with theunderlying steel.During thermal cycling at elevated temperatures (600-1000 °C) there occurs a statistically significant number of faults in cohesion and mechanical destruction of the coatings. One of the reasons are secondary changes

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2015: 24th International Conference on Metallurgy and Materials, Conference Proceedings

ISBN

978-80-87294-62-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1069-1074

Název nakladatele

TANGER Ltd

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

3. 6. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—