Structure of nanocrystalline nickel prepared by powder metallurgy

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F15%3A00473377" target="_blank" >RIV/61389021:_____/15:00473377 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.647.102" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.647.102</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.647.102" target="_blank" >10.4028/www.scientific.net/KEM.647.102</a>

Jazyk výsledku
angličtina
Název v původním jazyce
Structure of nanocrystalline nickel prepared by powder metallurgy
Popis výsledku v původním jazyce
Nanocrystalline nickel was prepared by selective leaching technology. Consequently, the powder was compacted by spark plasma sintering method. This process is suitable due to its high heating rates, which leads to relatively low thermal exposition of compacted material. The dependence of structure of compacted material on preparation conditions is described in this paper
Název v anglickém jazyce
Structure of nanocrystalline nickel prepared by powder metallurgy
Popis výsledku anglicky
Nanocrystalline nickel was prepared by selective leaching technology. Consequently, the powder was compacted by spark plasma sintering method. This process is suitable due to its high heating rates, which leads to relatively low thermal exposition of compacted material. The dependence of structure of compacted material on preparation conditions is described in this paper

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)