Corrosion behavior of plasma coatings CuAl10 and CuAl50 on magnesium alloy AZ 91

Popis výsledku v původním jazyce

The most common magnesium alloy AZ 91 is widely used as a structural material, but its use is limited at higher temperatures and high humidity. Plasma spraying is a technology that allows to prepare protective metallic and non-metallic coatings on a wide variety of substrates including magnesium and its alloys. In this study, CuAl10 and CuAl50 were plasma sprayed on magnesium alloy AZ 91 with the aim to study corrosion resistance of the plasma sprayed coatings. The corrosion resistance of layers was evaluated by the method of electrochemical potentiodynamic measurement as well as long-term corrosion tests in a condensation chamber with 0.5 molnNaCl at the temperature of 35 °C for 1344 hours. Layers with 1, 2, 5 passes and passes of CuAl10 with the thickness ranging from 75 to 716 mm and CuAl50 with the thickness ranging from 64 to 566 mm were prepared. The increased corrosion velocity was observed in the case of thin layers of 2 and 5 passes due to the development of a galvanic corrosion couple. The CuAl10 layer prepared with ten passes has an outstanding corrosion resistance.

Název v anglickém jazyce

Corrosion behavior of plasma coatings CuAl10 and CuAl50 on magnesium alloy AZ 91

Popis výsledku anglicky

The most common magnesium alloy AZ 91 is widely used as a structural material, but its use is limited at higher temperatures and high humidity. Plasma spraying is a technology that allows to prepare protective metallic and non-metallic coatings on a wide variety of substrates including magnesium and its alloys. In this study, CuAl10 and CuAl50 were plasma sprayed on magnesium alloy AZ 91 with the aim to study corrosion resistance of the plasma sprayed coatings. The corrosion resistance of layers was evaluated by the method of electrochemical potentiodynamic measurement as well as long-term corrosion tests in a condensation chamber with 0.5 molnNaCl at the temperature of 35 °C for 1344 hours. Layers with 1, 2, 5 passes and passes of CuAl10 with the thickness ranging from 75 to 716 mm and CuAl50 with the thickness ranging from 64 to 566 mm were prepared. The increased corrosion velocity was observed in the case of thin layers of 2 and 5 passes due to the development of a galvanic corrosion couple. The CuAl10 layer prepared with ten passes has an outstanding corrosion resistance.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP14-31538P" target="_blank" >GP14-31538P: Vývoj chemických vazeb na rozhraní během a po plazmovém stříkání kovových materiálů na hořčík a slitiny hořčíku</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the 4th International Conference on Chemical Technology

ISBN

978-80-86238-94-4

ISSN

2336-811X

e-ISSN

—

Počet stran výsledku

6

Strana od-do

259-264

Název nakladatele

Czech Society of Industrial Chemistry

Místo vydání

Prague

Místo konání akce

Mikulov

Datum konání akce

25. 4. 2016

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—