Spark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F16%3A00468777" target="_blank" >RIV/61389021:_____/16:00468777 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/16:10335279

Výsledek na webu

<a href="http://dx.doi.org/10.3390/ma9121004" target="_blank" >http://dx.doi.org/10.3390/ma9121004</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma9121004" target="_blank" >10.3390/ma9121004</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Spark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties

Popis výsledku v původním jazyce

The powder of an Al7075 alloy was prepared by gas atomization. A combination of cellular, columnar, and equiaxed dendritic-like morphology was observed in individual powder particles with continuous layers of intermetallic phases along boundaries. The cells are separated predominantly by high-angle boundaries, the areas with dendritic-like morphology usually have a similar crystallographic orientation. Spark plasma sintering resulted in a fully dense material with a microstructure similar to that of the powder material. The continuous layers of intermetallic phases are replaced by individual particles located along internal boundaries, coarse particles are formed at the surface of original powder particles. Microhardness measurements revealed both artificial and natural ageing behavior similar to that observed in ingot metallurgy material. The minimum microhardness of 81 HV, observed in the sample annealed at 300 °C, reflects the presence of coarse particles. The peak microhardness of 160 HV was observed in the sample annealed at 500 °C and then aged at room temperature. Compression tests confirmed high strength combined with sufficient plasticity. Annealing even at 500 °C does not significantly influence the distribution of grain sizes—about 45% of the area is occupied by grains with the size below 10 µm.

Název v anglickém jazyce

Spark Plasma Sintering of a Gas Atomized Al7075 Alloy: Microstructure and Properties

Popis výsledku anglicky

The powder of an Al7075 alloy was prepared by gas atomization. A combination of cellular, columnar, and equiaxed dendritic-like morphology was observed in individual powder particles with continuous layers of intermetallic phases along boundaries. The cells are separated predominantly by high-angle boundaries, the areas with dendritic-like morphology usually have a similar crystallographic orientation. Spark plasma sintering resulted in a fully dense material with a microstructure similar to that of the powder material. The continuous layers of intermetallic phases are replaced by individual particles located along internal boundaries, coarse particles are formed at the surface of original powder particles. Microhardness measurements revealed both artificial and natural ageing behavior similar to that observed in ingot metallurgy material. The minimum microhardness of 81 HV, observed in the sample annealed at 300 °C, reflects the presence of coarse particles. The peak microhardness of 160 HV was observed in the sample annealed at 500 °C and then aged at room temperature. Compression tests confirmed high strength combined with sufficient plasticity. Annealing even at 500 °C does not significantly influence the distribution of grain sizes—about 45% of the area is occupied by grains with the size below 10 µm.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JJ - Ostatní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA15-15609S" target="_blank" >GA15-15609S: Ultra-jemnozrnné a nanokrystalické kovové materiály s vysokou pevností připravené slinovaním pulzním elektrickým proudem</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

12

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

15

Strana od-do

—

Kód UT WoS článku

000390953400050

EID výsledku v databázi Scopus

2-s2.0-85007410618