Mechanical properties of plasma-sprayed layers of aluminium and aluminium alloy on AZ 91

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F17%3A00474333" target="_blank" >RIV/61389021:_____/17:00474333 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.17222/mit.2015.326" target="_blank" >http://dx.doi.org/10.17222/mit.2015.326</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.17222/mit.2015.326" target="_blank" >10.17222/mit.2015.326</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical properties of plasma-sprayed layers of aluminium and aluminium alloy on AZ 91

Popis výsledku v původním jazyce

Magnesium alloys are promising materials thanks to their high specific strength and stiffness. However, their wide application is discouraged by their low resistance to wear and very low resistance to corrosion. Plasma-spraying technology makes it possible to prepare protective metal and non-metal coatings. In this work, 450 .mu.m thick and 490 .mu.m thick plasma-spray coatings of commercially pure (CP) aluminium and aluminium alloy AlCr6Fe2 were prepared on magnesium alloy AZ91. The adhesion strength of plasma-sprayed aluminium was about 19 MPa, while the aluminium alloy showed an adhesion strength of about 12 MPa. Plasma-sprayed coatings improved the wear resistance of the AZ91 surface up to four times

Název v anglickém jazyce

Mechanical properties of plasma-sprayed layers of aluminium and aluminium alloy on AZ 91

Popis výsledku anglicky

Magnesium alloys are promising materials thanks to their high specific strength and stiffness. However, their wide application is discouraged by their low resistance to wear and very low resistance to corrosion. Plasma-spraying technology makes it possible to prepare protective metal and non-metal coatings. In this work, 450 .mu.m thick and 490 .mu.m thick plasma-spray coatings of commercially pure (CP) aluminium and aluminium alloy AlCr6Fe2 were prepared on magnesium alloy AZ91. The adhesion strength of plasma-sprayed aluminium was about 19 MPa, while the aluminium alloy showed an adhesion strength of about 12 MPa. Plasma-sprayed coatings improved the wear resistance of the AZ91 surface up to four times

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GP14-31538P" target="_blank" >GP14-31538P: Vývoj chemických vazeb na rozhraní během a po plazmovém stříkání kovových materiálů na hořčík a slitiny hořčíku</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials and Technology

ISSN

1580-2949

e-ISSN

—

Svazek periodika

51

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

5

Strana od-do

323-327

Kód UT WoS článku

000400203400020

EID výsledku v databázi Scopus

2-s2.0-85017395206