Behavior of the Steel T91 under Multi Axial Loading in Contact with Liquid and Solid Pb

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F17%3A00498209" target="_blank" >RIV/61389021:_____/17:00498209 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/17:N0000029

Výsledek na webu

<a href="https://www.mdpi.com/2075-4701/7/9/342" target="_blank" >https://www.mdpi.com/2075-4701/7/9/342</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/met7090342" target="_blank" >10.3390/met7090342</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Behavior of the Steel T91 under Multi Axial Loading in Contact with Liquid and Solid Pb

Popis výsledku v původním jazyce

In this work, the conditions for the occurrence of Liquid Metal Embrittlement (LME) in the ferritic-martensitic steel T91 in contact with lead, Pb, were examined. Slow tensile tests with notched specimens revealed that in a temperature range close to the melting point of Pb, the steel is sensitive to LME (350-400 °C) and to Solid Metal Induced Embrittlement (SMIE) (300 °C). The cracking was stimulated by wetting (using a chemical flux) and the notch effect. It was found that the multi axial stresses state and the high level of plastic strain in front of the notch were the key factors triggering crack initiation.

Název v anglickém jazyce

Behavior of the Steel T91 under Multi Axial Loading in Contact with Liquid and Solid Pb

Popis výsledku anglicky

In this work, the conditions for the occurrence of Liquid Metal Embrittlement (LME) in the ferritic-martensitic steel T91 in contact with lead, Pb, were examined. Slow tensile tests with notched specimens revealed that in a temperature range close to the melting point of Pb, the steel is sensitive to LME (350-400 °C) and to Solid Metal Induced Embrittlement (SMIE) (300 °C). The cracking was stimulated by wetting (using a chemical flux) and the notch effect. It was found that the multi axial stresses state and the high level of plastic strain in front of the notch were the key factors triggering crack initiation.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metals

ISSN

2075-4701

e-ISSN

—

Svazek periodika

7

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

14

Strana od-do

—

Kód UT WoS článku

000412063900021

EID výsledku v databázi Scopus

2-s2.0-85028927388