Tantalum Oxide Dielectrics Fired by Spark Plasma Sintering

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F18%3A00495674" target="_blank" >RIV/61389021:_____/18:00495674 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21230/18:00324268

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Tantalum Oxide Dielectrics Fired by Spark Plasma Sintering

Popis výsledku v původním jazyce

Tantalum pentoxide Ta2O5 was sintered by spark plasma sintering (SPS) using a commercial micrometric powder. Influence of the SPS process and subsequent annealing on microstructure, phase composition and dielectric properties was studied. After sintering the product is oxygen-deficient because of low pressure in the sintering chamber. The evacuation is necessary for the process because of carbon pistons and carbon die used for powder compaction. After subsequent annealing in air the color of the product Ta2O5 is restored that is proper indication of the re-oxidation. Dielectric properties were studied in a broad range of frequencies. Both as-sintered and annealed samples exhibit high relative permittivity about 61 to 68, loss factor about 0.001 and resistivity in order 10 E11 Ωm.

Název v anglickém jazyce

Tantalum Oxide Dielectrics Fired by Spark Plasma Sintering

Popis výsledku anglicky

Tantalum pentoxide Ta2O5 was sintered by spark plasma sintering (SPS) using a commercial micrometric powder. Influence of the SPS process and subsequent annealing on microstructure, phase composition and dielectric properties was studied. After sintering the product is oxygen-deficient because of low pressure in the sintering chamber. The evacuation is necessary for the process because of carbon pistons and carbon die used for powder compaction. After subsequent annealing in air the color of the product Ta2O5 is restored that is proper indication of the re-oxidation. Dielectric properties were studied in a broad range of frequencies. Both as-sintered and annealed samples exhibit high relative permittivity about 61 to 68, loss factor about 0.001 and resistivity in order 10 E11 Ωm.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of the EURO PM2018 – European powder metallurgy association (EPMA) Congress and Exhibition

ISBN

978-1-899072-50-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

European powder metallurgy association

Místo vydání

EPMA, Haughmond View, Sitka Drive, Shrewsburry

Místo konání akce

Bilbao

Datum konání akce

14. 10. 2018

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—