Different Types of Particle Effects in Creep Tests of CoCrFeNiMn High-Entropy Alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F22%3A00563745" target="_blank" >RIV/61389021:_____/22:00563745 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/22:00563745

Výsledek na webu

<a href="https://www.mdpi.com/1996-1944/15/20/7363" target="_blank" >https://www.mdpi.com/1996-1944/15/20/7363</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma15207363" target="_blank" >10.3390/ma15207363</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Different Types of Particle Effects in Creep Tests of CoCrFeNiMn High-Entropy Alloy

Popis výsledku v původním jazyce

Compressive creep tests were performed on a CoCrFeNiMn equiatomic alloy with the dispersion of (i) aluminum nitride or (ii) boron nitride at temperatures of 973 K and 1073 K. The results are compared with previously published creep rates of the unreinforced matrix alloy and the alloy when strengthened by yttrium + titanium oxides. The comparison reveals that the creep rate is essentially unchanged by the presence of aluminum nitride particles, whereas it is reduced by the presence of oxide particles. Boron nitride particles do not influence the creep rate at low stresses but reduce it substantially at high stresses.

Název v anglickém jazyce

Different Types of Particle Effects in Creep Tests of CoCrFeNiMn High-Entropy Alloy

Popis výsledku anglicky

Compressive creep tests were performed on a CoCrFeNiMn equiatomic alloy with the dispersion of (i) aluminum nitride or (ii) boron nitride at temperatures of 973 K and 1073 K. The results are compared with previously published creep rates of the unreinforced matrix alloy and the alloy when strengthened by yttrium + titanium oxides. The comparison reveals that the creep rate is essentially unchanged by the presence of aluminum nitride particles, whereas it is reduced by the presence of oxide particles. Boron nitride particles do not influence the creep rate at low stresses but reduce it substantially at high stresses.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

1996-1944

Svazek periodika

15

Číslo periodika v rámci svazku

20

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

8

Strana od-do

7363

Kód UT WoS článku

000873243900001

EID výsledku v databázi Scopus

2-s2.0-85140756957