Dielectric Properties of Lithium Fluoride Sintered After High-Pressure Forming

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F22%3A00571806" target="_blank" >RIV/61389021:_____/22:00571806 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21230/22:00362783

Výsledek na webu

<a href="http://dx.doi.org/10.1109/IWIS57888.2022.9975129" target="_blank" >http://dx.doi.org/10.1109/IWIS57888.2022.9975129</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1109/IWIS57888.2022.9975129" target="_blank" >10.1109/IWIS57888.2022.9975129</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Dielectric Properties of Lithium Fluoride Sintered After High-Pressure Forming

Popis výsledku v původním jazyce

The high pressure forming at 300 MPa and room temperature was applied before firing of pure lithium fluoride powder. This material has very low sintering temperature, only about one half of typical oxide-ceramic dielectrics. Despite this fact, the resulting fired bulk was tested as dielectrics and showed very interesting characteristics. The best sample, fired at 750 degrees C and for 8 hours, had relative permittivity 12.1 and loss tangent 0.0006, frequency- and temperature-independent up to at least 150 degrees C. These parameters are comparable with oxide ceramics, fired at temperatures over 1500 degrees C, as for example alumina or YAG.

Název v anglickém jazyce

Dielectric Properties of Lithium Fluoride Sintered After High-Pressure Forming

Popis výsledku anglicky

The high pressure forming at 300 MPa and room temperature was applied before firing of pure lithium fluoride powder. This material has very low sintering temperature, only about one half of typical oxide-ceramic dielectrics. Despite this fact, the resulting fired bulk was tested as dielectrics and showed very interesting characteristics. The best sample, fired at 750 degrees C and for 8 hours, had relative permittivity 12.1 and loss tangent 0.0006, frequency- and temperature-independent up to at least 150 degrees C. These parameters are comparable with oxide ceramics, fired at temperatures over 1500 degrees C, as for example alumina or YAG.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings of International Workshop on Impedance Spectroscopy

ISBN

979-835031039-9

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

(2022)

Název nakladatele

Institute of Electrical and Electronics Engineers Inc.

Místo vydání

Chemnitz

Místo konání akce

Chemnitz

Datum konání akce

27. 9. 2022

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000904772500022