Testing of ITER-grade plasma facing units in the WEST tokamak: Progress in understanding heat loading and damage mechanisms

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F23%3A00584102" target="_blank" >RIV/61389021:_____/23:00584102 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S2352179123001850?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2352179123001850?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.nme.2023.101546" target="_blank" >10.1016/j.nme.2023.101546</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Testing of ITER-grade plasma facing units in the WEST tokamak: Progress in understanding heat loading and damage mechanisms

Popis výsledku v původním jazyce

Assessing the performance of the ITER design for the tungsten (W) divertor Plasma Facing Units (PFUs) in a tokamak environment is a high priority issue to ensure efficient plasma operation. This paper reviews the most recent results derived from experiments and post-mortem analysis of the ITER-grade PFUs exposed in the WEST tokamak and the associated modelling, with a focus on understanding heat loading and damage evolution. Several shaping options, sharp or chamfered leading edge (LE), unshaped or shaped blocks with a toroidal bevel as foreseen in ITER, were investigated, under steady state heat fluxes of up to 120 MW⋅m−2 and 6 MW⋅m−2 on the sharp LE and top surface of the block, respectively. A very high spatial resolution (VHR) infrared (IR) camera (0.1 mm/pixel) was used to derive the temporal and surface distribution of the temperature and heat load on the castellated tungsten blocks for different geometric alignment and plasma conditions. Photonic modelling was required to reproduce the IR measurements in particular in the toroidal and poloidal gaps of the mono-block (MB) stacks where high apparent temperatures are observed. Specular reflection is found to be the dominant emitter in these parts of the blocks. W-cracking was observed on the leading edge of the blocks already within the first phase of plasma operation, during which the divertor was equipped with unshaped PFUs, including some intentionally misaligned blocks. Numerical analysis taking into account softening processes and mechanical stresses, revealed brittle failure due to transients as the dominant failure mechanisms. Ductile failure was observed in one particular block used for the melting experiment, therefore under extremely high steady state heat load conditions. W-melting achieved on actively cooled PFU exhibits specific features: shallow melting and slow melt displacement. Plasma exposure of pre-damaged PFUs at various damage levels (crack network and melted droplets) was carried out under high heat load conditions with several hours of cumulated plasma duration. IR data and preliminary surface analyses show no evidence of significant degradation damage progression under these conditions.

Název v anglickém jazyce

Testing of ITER-grade plasma facing units in the WEST tokamak: Progress in understanding heat loading and damage mechanisms

Popis výsledku anglicky

Assessing the performance of the ITER design for the tungsten (W) divertor Plasma Facing Units (PFUs) in a tokamak environment is a high priority issue to ensure efficient plasma operation. This paper reviews the most recent results derived from experiments and post-mortem analysis of the ITER-grade PFUs exposed in the WEST tokamak and the associated modelling, with a focus on understanding heat loading and damage evolution. Several shaping options, sharp or chamfered leading edge (LE), unshaped or shaped blocks with a toroidal bevel as foreseen in ITER, were investigated, under steady state heat fluxes of up to 120 MW⋅m−2 and 6 MW⋅m−2 on the sharp LE and top surface of the block, respectively. A very high spatial resolution (VHR) infrared (IR) camera (0.1 mm/pixel) was used to derive the temporal and surface distribution of the temperature and heat load on the castellated tungsten blocks for different geometric alignment and plasma conditions. Photonic modelling was required to reproduce the IR measurements in particular in the toroidal and poloidal gaps of the mono-block (MB) stacks where high apparent temperatures are observed. Specular reflection is found to be the dominant emitter in these parts of the blocks. W-cracking was observed on the leading edge of the blocks already within the first phase of plasma operation, during which the divertor was equipped with unshaped PFUs, including some intentionally misaligned blocks. Numerical analysis taking into account softening processes and mechanical stresses, revealed brittle failure due to transients as the dominant failure mechanisms. Ductile failure was observed in one particular block used for the melting experiment, therefore under extremely high steady state heat load conditions. W-melting achieved on actively cooled PFU exhibits specific features: shallow melting and slow melt displacement. Plasma exposure of pre-damaged PFUs at various damage levels (crack network and melted droplets) was carried out under high heat load conditions with several hours of cumulated plasma duration. IR data and preliminary surface analyses show no evidence of significant degradation damage progression under these conditions.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10305 - Fluids and plasma physics (including surface physics)

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Materials and Energy

ISSN

2352-1791

e-ISSN

2352-1791

Svazek periodika

37

Číslo periodika v rámci svazku

December

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

13

Strana od-do

101546

Kód UT WoS článku

001119119300001

EID výsledku v databázi Scopus

2-s2.0-85177591538