Using DOProC method in reliability assessment of steel elements exposed to fatigue
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27120%2F17%3A10237252" target="_blank" >RIV/61989100:27120/17:10237252 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.matec-conferences.org/articles/matecconf/abs/2017/21/matecconf_dyn2017_00046/matecconf_dyn2017_00046.html" target="_blank" >https://www.matec-conferences.org/articles/matecconf/abs/2017/21/matecconf_dyn2017_00046/matecconf_dyn2017_00046.html</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1051/matecconf/201710700046" target="_blank" >10.1051/matecconf/201710700046</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Using DOProC method in reliability assessment of steel elements exposed to fatigue
Popis výsledku v původním jazyce
Fatigue crack damage depends on a number of stress range cycles. This is a time factor in the course of reliability for the entire designed service life. Three sizes are important for the characteristics of the propagation of fatigue cracks - initial size, detectable size and acceptable size. The theoretical model of fatigue crack progression can be based on a linear fracture mechanic. Depending on location of an initial crack, the crack may propagate in structural element e.g. from the edge or from the surface. When determining the required degree of reliability, it is possible to specify the time of the first inspection of the construction which will focus on the fatigue damage. Using a conditional probability and Bayesian approach, times for subsequent inspections can be determined. For probabilistic modelling of fatigue crack progression was used the original and new probabilistic method - the Direct Optimized Probabilistic Calculation ("DOProC"), which uses a purely numerical approach without any simulation techniques or approximation approach based on optimized numerical integration.
Název v anglickém jazyce
Using DOProC method in reliability assessment of steel elements exposed to fatigue
Popis výsledku anglicky
Fatigue crack damage depends on a number of stress range cycles. This is a time factor in the course of reliability for the entire designed service life. Three sizes are important for the characteristics of the propagation of fatigue cracks - initial size, detectable size and acceptable size. The theoretical model of fatigue crack progression can be based on a linear fracture mechanic. Depending on location of an initial crack, the crack may propagate in structural element e.g. from the edge or from the surface. When determining the required degree of reliability, it is possible to specify the time of the first inspection of the construction which will focus on the fatigue damage. Using a conditional probability and Bayesian approach, times for subsequent inspections can be determined. For probabilistic modelling of fatigue crack progression was used the original and new probabilistic method - the Direct Optimized Probabilistic Calculation ("DOProC"), which uses a purely numerical approach without any simulation techniques or approximation approach based on optimized numerical integration.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20102 - Construction engineering, Municipal and structural engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GA17-01589S" target="_blank" >GA17-01589S: Pokročilé výpočetní a pravděpodobnostní modelování ocelových konstrukcí s ohledem na únavové poškození</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
MATEC Web of Conferences. Volume 107
ISBN
—
ISSN
2261-236X
e-ISSN
2261-236X
Počet stran výsledku
8
Strana od-do
1-8
Název nakladatele
EDP Sciences
Místo vydání
Paříž
Místo konání akce
Trstená
Datum konání akce
21. 5. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000407745800046