High-cycle fatigue cracks in concrete investigated by μcT tomography

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27120%2F23%3A10254055" target="_blank" >RIV/61989100:27120/23:10254055 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26110/23:PU147581
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S2452321622008095?pes=vor" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2452321622008095?pes=vor</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.prostr.2022.12.246" target="_blank" >10.1016/j.prostr.2022.12.246</a>

Jazyk výsledku
angličtina
Název v původním jazyce
High-cycle fatigue cracks in concrete investigated by μcT tomography
Popis výsledku v původním jazyce
This contribution deals with the analysis of fatigue damage in high-performance concrete (HPC) studied by three-point bending test. The concrete sample was tested with frequency of 10 Hz and it was exposed to a total number of load cycles 2x106. The internal structure and damage localization was studied by μCT tomography. Found locations of internal damage i.e., cracks, were discussed.
Název v anglickém jazyce
High-cycle fatigue cracks in concrete investigated by μcT tomography
Popis výsledku anglicky
This contribution deals with the analysis of fatigue damage in high-performance concrete (HPC) studied by three-point bending test. The concrete sample was tested with frequency of 10 Hz and it was exposed to a total number of load cycles 2x106. The internal structure and damage localization was studied by μCT tomography. Found locations of internal damage i.e., cracks, were discussed.

Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2023
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)