Impact of Freeze-thaw Cycles on Coatings Applied to the Surface of Alkali-activated Materials

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27120%2F24%3A10258484" target="_blank" >RIV/61989100:27120/24:10258484 - isvavai.cz</a>

Výsledek na webu

<a href="https://doi.org/10.5281/zenodo.11453028" target="_blank" >https://doi.org/10.5281/zenodo.11453028</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.29227/IM-2024-02-05" target="_blank" >10.29227/IM-2024-02-05</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Impact of Freeze-thaw Cycles on Coatings Applied to the Surface of Alkali-activated Materials

Popis výsledku v původním jazyce

This paper focuses on the possibility of applying selected types of coatings (synthetic and epoxy) on the surface of alkali-activated materials based on finely ground granulated blast furnace slag with an admixture of cement by-pass dust and silica fly ash. Admixtures represent 30% of the binder component (15% fly ash, 15% cement by-pass dust). The mixture is activated with anhydrous disodium metasilicate. The samples were categorized into two series samples stored in water and samples wrapped in foil. Following this, the surface of these two series was modified by two methods, namely brushing with a steel brush and roughening with a diamond wheel. The properties related to the adhesion of the coating to the surface were mainly investigated before and after 100 freeze-thaw cycles. The cross-cut method and pull-off test for adhesion determined the adhesion. The cross-cut test found that the synthetic coating was less susceptible to surface modification than the epoxy coating. The samples were exposed to 100 freeze-thaw cycles. Then, the cross-cut method was applied to the coated roughened surface and the results of this test were classified into category 3. During the determination of the adhesion of the coatings by the pull-off test on the roughened surface for both methods of sample storage, the character of breakage for the synthetic coating was of the cohesive type, thus it was the tensile strength of the materials, while for the epoxy coating, it was the adhesive breakage, thus it was the adhesion between the surface and the coating.

Název v anglickém jazyce

Impact of Freeze-thaw Cycles on Coatings Applied to the Surface of Alkali-activated Materials

Popis výsledku anglicky

This paper focuses on the possibility of applying selected types of coatings (synthetic and epoxy) on the surface of alkali-activated materials based on finely ground granulated blast furnace slag with an admixture of cement by-pass dust and silica fly ash. Admixtures represent 30% of the binder component (15% fly ash, 15% cement by-pass dust). The mixture is activated with anhydrous disodium metasilicate. The samples were categorized into two series samples stored in water and samples wrapped in foil. Following this, the surface of these two series was modified by two methods, namely brushing with a steel brush and roughening with a diamond wheel. The properties related to the adhesion of the coating to the surface were mainly investigated before and after 100 freeze-thaw cycles. The cross-cut method and pull-off test for adhesion determined the adhesion. The cross-cut test found that the synthetic coating was less susceptible to surface modification than the epoxy coating. The samples were exposed to 100 freeze-thaw cycles. Then, the cross-cut method was applied to the coated roughened surface and the results of this test were classified into category 3. During the determination of the adhesion of the coatings by the pull-off test on the roughened surface for both methods of sample storage, the character of breakage for the synthetic coating was of the cohesive type, thus it was the tensile strength of the materials, while for the epoxy coating, it was the adhesive breakage, thus it was the adhesion between the surface and the coating.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

O - Projekt operacniho programu

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Inżynieria Mineralna

ISSN

1640-4920

e-ISSN

1640-4920

Svazek periodika

2

Číslo periodika v rámci svazku

54

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

7

Strana od-do

28-34

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-105023188033