Contribution to research of weldability of modern low-alloy creep resistant steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F03%3A00008949" target="_blank" >RIV/61989100:27230/03:00008949 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Contribution to research of weldability of modern low-alloy creep resistant steels

Popis výsledku v původním jazyce

This article presents the results of weldability tests performed on T23, T24 and T25 steels. Based on these test results a suitable preheating temperature was calculated for welding the said steels of 6 to 20 mm thickness. Further, this article deals with hardening of weld joints in perspective steels T23 and T24 during extensive exposure at operating temperature 500 °C. The extent of secondary hardening depends on application of tempering after welding. Non-tempered weld joints undergo an unacceptableincrease in hardness during exposure at operating temperature. Based on test results a suitable temperature profile was calculated for welding membrane walls from T23 and T24 steels.

Název v anglickém jazyce

Contribution to research of weldability of modern low-alloy creep resistant steels

Popis výsledku anglicky

This article presents the results of weldability tests performed on T23, T24 and T25 steels. Based on these test results a suitable preheating temperature was calculated for welding the said steels of 6 to 20 mm thickness. Further, this article deals with hardening of weld joints in perspective steels T23 and T24 during extensive exposure at operating temperature 500 °C. The extent of secondary hardening depends on application of tempering after welding. Non-tempered weld joints undergo an unacceptableincrease in hardness during exposure at operating temperature. Based on test results a suitable temperature profile was calculated for welding membrane walls from T23 and T24 steels.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LN00B029" target="_blank" >LN00B029: Materiálově technologické výzkumné centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2003

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

6

Strana od-do

210-216

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—