Influence of Li Kation on Electrodeposition of Nickel - Iron and Nickel - Kobalt Alloys

Popis výsledku v původním jazyce

The cation Li+ ,which does not take a direct part on the process of electrodeposition of iron group metals, may affect that process due to its ability of adsorption on the cathode surface. A lower hydrogen content has been proved in the case of nickel-iron alloys, what should lead to lower internal stress in particular cases. A comparison between two alloying metals, i.e. iron and cobalt has been carried out as far as internal stress is concerned. The positive effect of lithium on internal stress in thecase of nickel-iron alloys has been proved, while a similar effect is dubious in the case of alloys nickel-cobalt. Nevertheless, these types of alloys are acceptable from a practical point of view in the both cases, as the level of internal stress doesnot exceed 150 MPa in some range of cathodic current densities.

Název v anglickém jazyce

Influence of Li Kation on Electrodeposition of Nickel - Iron and Nickel - Kobalt Alloys

Popis výsledku anglicky

The cation Li+ ,which does not take a direct part on the process of electrodeposition of iron group metals, may affect that process due to its ability of adsorption on the cathode surface. A lower hydrogen content has been proved in the case of nickel-iron alloys, what should lead to lower internal stress in particular cases. A comparison between two alloying metals, i.e. iron and cobalt has been carried out as far as internal stress is concerned. The positive effect of lithium on internal stress in thecase of nickel-iron alloys has been proved, while a similar effect is dubious in the case of alloys nickel-cobalt. Nevertheless, these types of alloys are acceptable from a practical point of view in the both cases, as the level of internal stress doesnot exceed 150 MPa in some range of cathodic current densities.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0951" target="_blank" >GA106/03/0951: Submikronové kompozitní soustavy s katodicky vylučovanou matricí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník abstraktů z mezinárodní konference Metal 2004

ISBN

80-85988-95-X

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

8

Název nakladatele

Tanger s.r.o.

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

18. 5. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—