Effect of thermal treatment and strain rate on superelastic and mechanical properties of NiTi sheet

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27230%2F23%3A10253832" target="_blank" >RIV/61989100:27230/23:10253832 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/23:10253832

Výsledek na webu

<a href="https://iopscience.iop.org/article/10.1088/1742-6596/2572/1/012008" target="_blank" >https://iopscience.iop.org/article/10.1088/1742-6596/2572/1/012008</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1088/1742-6596/2572/1/012008" target="_blank" >10.1088/1742-6596/2572/1/012008</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of thermal treatment and strain rate on superelastic and mechanical properties of NiTi sheet

Popis výsledku v původním jazyce

In this work, the influence of the heat treatment and the strain rate on the superelastic properties of the NiTi alloy was studied in the tensile testing. Thin NiTi sheets with a thickness of 2.0 mm and a content of 56.31 Ni and 43.69 Ti (in wt. %) were tested in different heat-treated conditions. The flat specimens were tensile tested at two different strain rates at the state as-received, after aging at 450 oC and after solution treatment at 850 oC followed by aging at 450 oC. The microstructure and phase analyses of the NiTi specimens in three heat-treated conditions were examined using optical and scanning electronic microscopies and were related to the superelastic behavior.

Název v anglickém jazyce

Effect of thermal treatment and strain rate on superelastic and mechanical properties of NiTi sheet

Popis výsledku anglicky

In this work, the influence of the heat treatment and the strain rate on the superelastic properties of the NiTi alloy was studied in the tensile testing. Thin NiTi sheets with a thickness of 2.0 mm and a content of 56.31 Ni and 43.69 Ti (in wt. %) were tested in different heat-treated conditions. The flat specimens were tensile tested at two different strain rates at the state as-received, after aging at 450 oC and after solution treatment at 850 oC followed by aging at 450 oC. The microstructure and phase analyses of the NiTi specimens in three heat-treated conditions were examined using optical and scanning electronic microscopies and were related to the superelastic behavior.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

<a href="/cs/project/FV40306" target="_blank" >FV40306: Vývoj nových implantátů pro regulaci růstu dolní končetiny ve sterilním provedení</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Journal of Physics: Conference Series. Volume 2572

ISBN

—

ISSN

1742-6588

e-ISSN

1742-6596

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

IOP Publishing

Místo vydání

Bristol

Místo konání akce

Plzeň

Datum konání akce

6. 9. 2022

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—