Influence of microstructure on fracture feature of Ti6Al4V alloy prepared by 3D printing
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27240%2F20%3A10244344" target="_blank" >RIV/61989100:27240/20:10244344 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61989100:27360/20:10244344
Výsledek na webu
<a href="http://dx.doi.org/10.1088/1757-899X/726/1/012020" target="_blank" >http://dx.doi.org/10.1088/1757-899X/726/1/012020</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1757-899X/726/1/012020" target="_blank" >10.1088/1757-899X/726/1/012020</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of microstructure on fracture feature of Ti6Al4V alloy prepared by 3D printing
Popis výsledku v původním jazyce
In this work, the Ti6Al4V specimens produced by selective laser melting were mechanically tested in non-heat treated condition and fracture surface features were compared with this one of the material prepared using conventional casting and forging. The results of the fractography observation for both types of the samples were explained on the base of the microstructure analysis. The fracture surface of selective laser melted specimens showed more brittle feature that was in relation with the microstructure composed almost fully of martensite as opposed to conventionally prepared alloy with bimodal (α + β) microstructure and more ductile character of fracture surfaces. (C) Published under licence by IOP Publishing Ltd.
Název v anglickém jazyce
Influence of microstructure on fracture feature of Ti6Al4V alloy prepared by 3D printing
Popis výsledku anglicky
In this work, the Ti6Al4V specimens produced by selective laser melting were mechanically tested in non-heat treated condition and fracture surface features were compared with this one of the material prepared using conventional casting and forging. The results of the fractography observation for both types of the samples were explained on the base of the microstructure analysis. The fracture surface of selective laser melted specimens showed more brittle feature that was in relation with the microstructure composed almost fully of martensite as opposed to conventionally prepared alloy with bimodal (α + β) microstructure and more ductile character of fracture surfaces. (C) Published under licence by IOP Publishing Ltd.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20500 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/FV40306" target="_blank" >FV40306: Vývoj nových implantátů pro regulaci růstu dolní končetiny ve sterilním provedení</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
IOP Conference Series: Materials Science and Engineering. Volume 726
ISBN
—
ISSN
1757-8981
e-ISSN
1757-899X
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
IOP Publishing
Místo vydání
Bristol
Místo konání akce
Nová Lesná
Datum konání akce
2. 9. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—