Preparation and Physical Properties of Quaternary Mn2FeSi0.5Al0.5 Alloy Powders with Heusler and β-Mn Structures

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27240%2F25%3A10257112" target="_blank" >RIV/61989100:27240/25:10257112 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61989100:27360/25:10257112

Výsledek na webu

<a href="https://www.mdpi.com/1996-1944/18/2/309" target="_blank" >https://www.mdpi.com/1996-1944/18/2/309</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma18020309" target="_blank" >10.3390/ma18020309</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation and Physical Properties of Quaternary Mn2FeSi0.5Al0.5 Alloy Powders with Heusler and β-Mn Structures

Popis výsledku v původním jazyce

Manganese-based alloys with the composition Mn2FeZ (Z = Si, Al) have been extensively investigated in recent years due to their potential applications in spintronics. The Mn2FeSi alloy, prepared in the form of ingots, powders, or ribbons, exhibits either a cubic full-Heusler (L21) structure, an inverse-Heusler (XA) structure, or a combination of both. In contrast, the Mn2FeAl alloy has so far been synthesized only in the form of ingots, featuring a primitive cubic (β-Mn type) structure. This study focuses on the new quaternary Mn2FeSi0.5Al0.5 alloy synthesized from pure Mn, Fe, Si, and Al powders via mechanical alloying. The elemental powders were ball-milled for 168 h with a ball-to-powder ratio of 10:1, followed by annealing at 550 °C, 700 °C, and 950 °C for 8 h in an argon protective atmosphere. The results demonstrate that annealing at lower temperatures (550 °C) led to the formation of a Heusler structure with a lattice constant of 0.5739 nm. Annealing at 700 °C resulted in the coexistence of several phases, including the Heusler phase and a newly developed primitive cubic β-Mn structure. Further increasing the annealing temperature to 950 °C completely suppressed the Heusler phase, with the β-Mn structure, having a lattice constant of 0.6281 nm, becoming the dominant phase. These findings confirm the possibility of tuning the structure of Mn2FeSi0.5Al0.5 alloy powder—and thereby its physical properties—by varying the annealing temperature. The sensitivity of magnetic properties to structural changes is demonstrated through magnetization curves and zero-field-cooled/field-cooled curves in the temperature range of 5 K to 300 K. © 2025 by the authors.

Název v anglickém jazyce

Preparation and Physical Properties of Quaternary Mn2FeSi0.5Al0.5 Alloy Powders with Heusler and β-Mn Structures

Popis výsledku anglicky

Manganese-based alloys with the composition Mn2FeZ (Z = Si, Al) have been extensively investigated in recent years due to their potential applications in spintronics. The Mn2FeSi alloy, prepared in the form of ingots, powders, or ribbons, exhibits either a cubic full-Heusler (L21) structure, an inverse-Heusler (XA) structure, or a combination of both. In contrast, the Mn2FeAl alloy has so far been synthesized only in the form of ingots, featuring a primitive cubic (β-Mn type) structure. This study focuses on the new quaternary Mn2FeSi0.5Al0.5 alloy synthesized from pure Mn, Fe, Si, and Al powders via mechanical alloying. The elemental powders were ball-milled for 168 h with a ball-to-powder ratio of 10:1, followed by annealing at 550 °C, 700 °C, and 950 °C for 8 h in an argon protective atmosphere. The results demonstrate that annealing at lower temperatures (550 °C) led to the formation of a Heusler structure with a lattice constant of 0.5739 nm. Annealing at 700 °C resulted in the coexistence of several phases, including the Heusler phase and a newly developed primitive cubic β-Mn structure. Further increasing the annealing temperature to 950 °C completely suppressed the Heusler phase, with the β-Mn structure, having a lattice constant of 0.6281 nm, becoming the dominant phase. These findings confirm the possibility of tuning the structure of Mn2FeSi0.5Al0.5 alloy powder—and thereby its physical properties—by varying the annealing temperature. The sensitivity of magnetic properties to structural changes is demonstrated through magnetization curves and zero-field-cooled/field-cooled curves in the temperature range of 5 K to 300 K. © 2025 by the authors.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

<a href="/cs/project/GA21-05339S" target="_blank" >GA21-05339S: Strukturní a fyzikální aspekty inverzních Heuslerových slitin Mn2FeZ, Z = Si, Al, Sn</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

1996-1944

Svazek periodika

18

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

15

Strana od-do

nestránkováno

Kód UT WoS článku

001404368500001

EID výsledku v databázi Scopus

2-s2.0-85216801192