The effect of CO2 on the strength characteristics of cement composites based on recycled rubber from waste tires
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27350%2F20%3A10245543" target="_blank" >RIV/61989100:27350/20:10245543 - isvavai.cz</a>
Výsledek na webu
<a href="https://iopscience.iop.org/article/10.1088/1757-899X/867/1/012042" target="_blank" >https://iopscience.iop.org/article/10.1088/1757-899X/867/1/012042</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1088/1757-899X/867/1/012042" target="_blank" >10.1088/1757-899X/867/1/012042</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The effect of CO2 on the strength characteristics of cement composites based on recycled rubber from waste tires
Popis výsledku v původním jazyce
This paper presents the results of a research into the use of a combination of recycled rubber from waste tires as a 100% aggregate replacement in the production of cement composites. The aggregate was replaced with rubber recycled material in two ratios. At a ratio of 50/50 and a ratio of 40/60 fraction 0/1 mm and fraction 1/3 mm. The test specimens were further subjected to CO2 effect in a Lamart laboratory chamber, where CO2 effect was simulated as equivalent to an aging period of 50 years. The presented results show that the effect of CO2 reduces the strength characteristics of the composite compared to the comparative samples. (C) Published under licence by IOP Publishing Ltd.
Název v anglickém jazyce
The effect of CO2 on the strength characteristics of cement composites based on recycled rubber from waste tires
Popis výsledku anglicky
This paper presents the results of a research into the use of a combination of recycled rubber from waste tires as a 100% aggregate replacement in the production of cement composites. The aggregate was replaced with rubber recycled material in two ratios. At a ratio of 50/50 and a ratio of 40/60 fraction 0/1 mm and fraction 1/3 mm. The test specimens were further subjected to CO2 effect in a Lamart laboratory chamber, where CO2 effect was simulated as equivalent to an aging period of 50 years. The presented results show that the effect of CO2 reduces the strength characteristics of the composite compared to the comparative samples. (C) Published under licence by IOP Publishing Ltd.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20700 - Environmental engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
IOP Conference Series: Materials Science and Engineering
ISBN
—
ISSN
1757-8981
e-ISSN
—
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
Institute of Physics
Místo vydání
London
Místo konání akce
Štrbské Pleso, the High Tatras, Slovakia.
Datum konání akce
15. 10. 2020
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—