The Hydrogen Embrittlement of C-Mn Steels

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F02%3A00001688" target="_blank" >RIV/61989100:27360/02:00001688 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The Hydrogen Embrittlement of C-Mn Steels

Popis výsledku v původním jazyce

Evaluation of susceptibility of C-Mn steels to hydrogen embrittlement were studied in this paper. Tensile tests performed on previously electrolytically charged specimens were used in this work. The specimens were taken in three decisive directions regarding to the plate rolling, i.e. in longitudinal and transversal directions as well as in through-thickness direction. It was found out that the level of hydrogen embrittlement (HE) displays expressive anisotropy and HE is increasing from longitudinal direction through transversal direction. Using stereomicroscope or scanning electron the microscope fish eyes can be observed on fracture areas of specimen after hydrogen electrolytical charging and tensile testing with low-speed deformation.

Název v anglickém jazyce

The Hydrogen Embrittlement of C-Mn Steels

Popis výsledku anglicky

Evaluation of susceptibility of C-Mn steels to hydrogen embrittlement were studied in this paper. Tensile tests performed on previously electrolytically charged specimens were used in this work. The specimens were taken in three decisive directions regarding to the plate rolling, i.e. in longitudinal and transversal directions as well as in through-thickness direction. It was found out that the level of hydrogen embrittlement (HE) displays expressive anisotropy and HE is increasing from longitudinal direction through transversal direction. Using stereomicroscope or scanning electron the microscope fish eyes can be observed on fracture areas of specimen after hydrogen electrolytical charging and tensile testing with low-speed deformation.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F00%2F0042" target="_blank" >GA106/00/0042: Hodnocení vodíkové křehkosti ocelí pomocí kvantitativních metod strukturní analýzy</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2002

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Development of Materials Science in Research and Education

ISBN

80-85912-85-8

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

3-4

Název nakladatele

MAXDORF, s.r.o.

Místo vydání

Praha

Místo konání akce

Ostravice

Datum konání akce

10. 9. 2002

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—