ANALYSIS OF ACICULAR FERRITE FORMATION IN HAZ OF PIPE-LINES STEEL AFTER HIGH HEAT INPUT WELDING

Popis výsledku v původním jazyce

The Ti adding to low-carbon steel leads to the microstructure modification from side plate ferrite (Widmanstätten ferrite, upper bainite) to acicular ferrite. The study has been carried out to classify the effect of acicular ferrite formation on toughness improvement of heat affected zone in large heat input welding (simulation process). The formation of intragranularly nucleated ferrite in heat effected zone results in improvement in material response. The steel after Ti-adding contains non-metallic inclusions of Ti2O3-type. These inclusions have dense cation vacancies what contributes greatly to preferential nucleation of various faces adhered with Ti2O3 (increase of Ti2O3 nucleation potency). This inclusion acts as preferential nucleation site of MnS and TiN. Precipitation of MnS results in a formation of Mn-depleted zone at Ti2O3/ferrite interface. This zone has higher chemical free enthalpy change for ferrite nucleation. TiN decreases interfacial energy for ferrite nucleation. The

Název v anglickém jazyce

ANALYSIS OF ACICULAR FERRITE FORMATION IN HAZ OF PIPE-LINES STEEL AFTER HIGH HEAT INPUT WELDING

Popis výsledku anglicky

The Ti adding to low-carbon steel leads to the microstructure modification from side plate ferrite (Widmanstätten ferrite, upper bainite) to acicular ferrite. The study has been carried out to classify the effect of acicular ferrite formation on toughness improvement of heat affected zone in large heat input welding (simulation process). The formation of intragranularly nucleated ferrite in heat effected zone results in improvement in material response. The steel after Ti-adding contains non-metallic inclusions of Ti2O3-type. These inclusions have dense cation vacancies what contributes greatly to preferential nucleation of various faces adhered with Ti2O3 (increase of Ti2O3 nucleation potency). This inclusion acts as preferential nucleation site of MnS and TiN. Precipitation of MnS results in a formation of Mn-depleted zone at Ti2O3/ferrite interface. This zone has higher chemical free enthalpy change for ferrite nucleation. TiN decreases interfacial energy for ferrite nucleation. The

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0264" target="_blank" >GA106/03/0264: Přenosové jevy při tuhnutí a jejich vliv na užitné vlastnosti materiálu</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

"Advanced metallic materials and their joining"

ISBN

5562-3162

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

1-5

Název nakladatele

VÚZ Bratislava

Místo vydání

Bratislava

Místo konání akce

Bratislava

Datum konání akce

25. 10. 2004

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—