Kvantitativní popis Kirkendallova vlivu ve spoji slitiny Ni3Al a niklu

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F04%3A00010232" target="_blank" >RIV/61989100:27360/04:00010232 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Quantitative description of Kirkendall's effect in bonded joints of Ni3Al alloy and nickel.

Popis výsledku v původním jazyce

Performed are the qualitative and quantitative metallographic examinations of bonded joints of the Ni3Al alloy on intermetallic phase matrix with pure Ni executed by means of electron beam. To simulate the working conditions for joints of this type, thesamples were annealed at temperature of 11400C for 48 h, 96 h and 192 h.There were observed structures typical for bonded joints: a polycrystalline native material, narrow heat affected zone and a weld area. An equiaxial polycrystalline structure of joint was disclosed after annealing. In the joint area was discovered occurrence of voids (i.e. Kirkendall's Effect), what confirms a vacancy nature of atomic diffusion in Ni3Al-Ni joints. Changes of shape and size of Kirkenadall's voids in the weld area aredescribed by means of stereological parameters.

Název v anglickém jazyce

Quantitative description of Kirkendall's effect in bonded joints of Ni3Al alloy and nickel.

Popis výsledku anglicky

Performed are the qualitative and quantitative metallographic examinations of bonded joints of the Ni3Al alloy on intermetallic phase matrix with pure Ni executed by means of electron beam. To simulate the working conditions for joints of this type, thesamples were annealed at temperature of 11400C for 48 h, 96 h and 192 h.There were observed structures typical for bonded joints: a polycrystalline native material, narrow heat affected zone and a weld area. An equiaxial polycrystalline structure of joint was disclosed after annealing. In the joint area was discovered occurrence of voids (i.e. Kirkendall's Effect), what confirms a vacancy nature of atomic diffusion in Ni3Al-Ni joints. Changes of shape and size of Kirkenadall's voids in the weld area aredescribed by means of stereological parameters.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Inżynieria Materiałowa, XVII Physical Metallurgy and Materials Science Conference "Advanced Materials and Technologies" (AMT´2004)

ISBN

0208-6247

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

698-701

Název nakladatele

SIGMA-NOT

Místo vydání

Lódź,Polsko

Místo konání akce

Lódź,Polsko

Datum konání akce

22. 6. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—