Nepříznivé vlivy vodíku na konstrukční oceli

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F04%3A00010808" target="_blank" >RIV/61989100:27360/04:00010808 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Hydrogen - Damage Effect on Structural Steels

Popis výsledku v původním jazyce

The severity of hydrogen deleterious effects depends on strength level, chemical composition, impurity content, and microstructure of structural steels. Harmful hydrogen effects on structural steels include: decrease of ductility as measured by elongation at fracture, and reduction of area, in particular at slow strain rates and at temperatures about room temperature; delayed failure under a static load; enhancement of the rate of propagation of a pre-existing crack; reduced fatigue strength; stress corrosion cracking in some form (SSC and HIC); blistering; hydrogen attack. All of these effects ultimately lead to lowering of the amount of externally applied load, energy or work necessary to produce material failure.In the present paper, the effects ofHIC and SSC are discussed. These effects can result from corrosion - generated hydrogen. Because the absorption of such hydrogen is greatly enhanced by sulphide - bearing waters is particularly conducive to hydrogen embrittlement (HE). Th

Název v anglickém jazyce

Hydrogen - Damage Effect on Structural Steels

Popis výsledku anglicky

The severity of hydrogen deleterious effects depends on strength level, chemical composition, impurity content, and microstructure of structural steels. Harmful hydrogen effects on structural steels include: decrease of ductility as measured by elongation at fracture, and reduction of area, in particular at slow strain rates and at temperatures about room temperature; delayed failure under a static load; enhancement of the rate of propagation of a pre-existing crack; reduced fatigue strength; stress corrosion cracking in some form (SSC and HIC); blistering; hydrogen attack. All of these effects ultimately lead to lowering of the amount of externally applied load, energy or work necessary to produce material failure.In the present paper, the effects ofHIC and SSC are discussed. These effects can result from corrosion - generated hydrogen. Because the absorption of such hydrogen is greatly enhanced by sulphide - bearing waters is particularly conducive to hydrogen embrittlement (HE). Th

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0235" target="_blank" >GA106/04/0235: Sulfidické praskání pod napětím moderních konstrukčních ocelí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník anotací Česko - Slovensko - Polské konference studentské tvůrčí činnosti

ISBN

0041-0634

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

25

Název nakladatele

ČVUT, FS, Ústav výrobních strojů a mechanismů

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

16. 6. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—