Influence of microstructure on SSC resistence of duplex steel 22/05

Popis výsledku v původním jazyce

This paper summarises results of SSC (Sulphide Stress Cracking) resistance of the duplex austenite-ferrite steel of type 22/05 with designation 22.5.3 according to the EURONORM 1.4462-X2CrNiMoN. Steel was tested in two different states. First of all in the as-received state after rolling and secondly after annealing to the following regime: 675oC/5h/air, which produced a discontinuous precipitation of the phase &#963;. The aim of this work was to show that resistance of steel to SSC depends strongly onthe microstructure (precipitation of minority phases in our case) and other metallurgical factors such as chemical composition and heat treatment. The resistance can't be derived only from material hardness, which is a common engineering approach. If this fact is not respected, a material non resistant to SSC can be chosen.

Název v anglickém jazyce

Influence of microstructure on SSC resistence of duplex steel 22/05

Popis výsledku anglicky

This paper summarises results of SSC (Sulphide Stress Cracking) resistance of the duplex austenite-ferrite steel of type 22/05 with designation 22.5.3 according to the EURONORM 1.4462-X2CrNiMoN. Steel was tested in two different states. First of all in the as-received state after rolling and secondly after annealing to the following regime: 675oC/5h/air, which produced a discontinuous precipitation of the phase &#963;. The aim of this work was to show that resistance of steel to SSC depends strongly onthe microstructure (precipitation of minority phases in our case) and other metallurgical factors such as chemical composition and heat treatment. The resistance can't be derived only from material hardness, which is a common engineering approach. If this fact is not respected, a material non resistant to SSC can be chosen.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0949" target="_blank" >GA106/04/0949: Mechanismy zvýšení korozní odolnosti vybraných ocelí po plazmové nitridaci a oxidaci</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Trends in the Development of Machinery and Associated Technology 2005

ISBN

9958-617-28-5

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

805-808

Název nakladatele

Faculty of Mechanical Engineering in Zenica, Bahcesehir University Istanbul, Turkey E.T.S.E.I. de Barcelona, Spain

Místo vydání

DOM ŠTAMBE Zenica

Místo konání akce

Antalya, Turkey

Datum konání akce

26. 9. 2005

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—