Vliv tepla během svařování na místní korozi korozivzdorných ocelí

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00013045" target="_blank" >RIV/61989100:27360/05:00013045 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Efect of heat during velding on localized corrosion of stainless steel

Popis výsledku v původním jazyce

The main factors which directly determine the thermal load in the weld are: the quantity of heat supplied, the welding method and the thermophysical values of the base metal. Since the corrosion characteristics of welds are closely connected with the thermal conditions, in the weld metal and base metal, much attention has been given to these conditions, especially in connection with the most widely used austenitic stainless steels. Carbidic precipitation and structural changes at elevated temperatures that markedly affect the susceptibility of austenitic CrNi welded stabilized stainless steels to intercrystalline corrosion, knife-line and/or fissure attack and others in the fusion line zones are considered

Název v anglickém jazyce

Efect of heat during velding on localized corrosion of stainless steel

Popis výsledku anglicky

The main factors which directly determine the thermal load in the weld are: the quantity of heat supplied, the welding method and the thermophysical values of the base metal. Since the corrosion characteristics of welds are closely connected with the thermal conditions, in the weld metal and base metal, much attention has been given to these conditions, especially in connection with the most widely used austenitic stainless steels. Carbidic precipitation and structural changes at elevated temperatures that markedly affect the susceptibility of austenitic CrNi welded stabilized stainless steels to intercrystalline corrosion, knife-line and/or fissure attack and others in the fusion line zones are considered

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F1188" target="_blank" >GA106/04/1188: Oplimalizace protikorozní ochrany v agresivních podmínkách spalin</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

European Corrosion Congres - EUROCORR 2005

ISBN

972-95921-2-8

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

52-59

Název nakladatele

SPM - Societ. Portugueza de Materials

Místo vydání

Lisabon

Místo konání akce

Lisabon

Datum konání akce

4. 9. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—