VLIV PODMÍNEK ZKOUŠENÍ NA SULFIDICKÉ PRASKÁNÍ POD NAPĚTÍM OCELÍ X52 A X60 DLE API

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014088" target="_blank" >RIV/61989100:27360/06:00014088 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

ROLE OF TESTING CONDITIONS IN SULPHIDE STRESS CRACKING OF X52 AND X60 API STEELS

Popis výsledku v původním jazyce

Resistance of X52 and X60 API steels to sulphide stress cracking (SSC) was tested by means of tensile tests at a constant load below the yield strength and also by means of slow strain rate tensile tests (SSRT). Both steels were tested in two different states, after hot rolling and after laboratory quenching and tempering. The results showed that steel resistance to SSC depended strongly on the microstructure when tests at the constant load were performed. In this case, quenching and tempering increasedsteel resistance to SSC considerably. The results of SSRT were different: they were similar regardless of the heat treatment. On the other hand, degree of degradation depended strongly on specimen orientation. Non-metallic inclusions seemed to play an important role as crack initiation sites during SSRT.

Název v anglickém jazyce

ROLE OF TESTING CONDITIONS IN SULPHIDE STRESS CRACKING OF X52 AND X60 API STEELS

Popis výsledku anglicky

Resistance of X52 and X60 API steels to sulphide stress cracking (SSC) was tested by means of tensile tests at a constant load below the yield strength and also by means of slow strain rate tensile tests (SSRT). Both steels were tested in two different states, after hot rolling and after laboratory quenching and tempering. The results showed that steel resistance to SSC depended strongly on the microstructure when tests at the constant load were performed. In this case, quenching and tempering increasedsteel resistance to SSC considerably. The results of SSRT were different: they were similar regardless of the heat treatment. On the other hand, degree of degradation depended strongly on specimen orientation. Non-metallic inclusions seemed to play an important role as crack initiation sites during SSRT.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0235" target="_blank" >GA106/04/0235: Sulfidické praskání pod napětím moderních konstrukčních ocelí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Acta Metallurgica Slovaca

ISBN

ISSN 1335-1532

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

462-468

Název nakladatele

Hutnická fakulta, Technická univerzita Košice

Místo vydání

Košice

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—