Evaluation of Corrosion of Refractory Materials by Molten Steel

Popis výsledku v původním jazyce

Works were solved in the frame of grant projects GACR reg. Nos. 106/04/0024 and 106/06/0393 and they were oriented on the study of corrosion phenomena of refractory materials, especially on interface refractory material - molten steel. Evaluation procedure was designed and experiments were done, which had to simulate in laboratory the conditions reached in plant. Results obtained in this manner make possible to evaluate influence of steel corrosion effects on refractory material. Visual evaluation of stressed refractory material after experiments was done and consequently structure micro-analysis of stressed refractory material was determined with focus on evaluation of metal penetration into the refractory material. Roentgen phase analysis was done asnext, individual crystallic phases are identified by means of this analysis. Assessment of metallographic cleanness of steel before and after contact with refractory material and assessment of rate of its corrosion, erosion and possibili

Název v anglickém jazyce

Evaluation of Corrosion of Refractory Materials by Molten Steel

Popis výsledku anglicky

Works were solved in the frame of grant projects GACR reg. Nos. 106/04/0024 and 106/06/0393 and they were oriented on the study of corrosion phenomena of refractory materials, especially on interface refractory material - molten steel. Evaluation procedure was designed and experiments were done, which had to simulate in laboratory the conditions reached in plant. Results obtained in this manner make possible to evaluate influence of steel corrosion effects on refractory material. Visual evaluation of stressed refractory material after experiments was done and consequently structure micro-analysis of stressed refractory material was determined with focus on evaluation of metal penetration into the refractory material. Roentgen phase analysis was done asnext, individual crystallic phases are identified by means of this analysis. Assessment of metallographic cleanness of steel before and after contact with refractory material and assessment of rate of its corrosion, erosion and possibili

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0024" target="_blank" >GA106/04/0024: Možnosti využití mezipánve a mezipánvové metalurgie při zvyšování čistoty oceli a jakosti náročných plochých výrobků</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metalurgija

ISSN

0543-5846

e-ISSN

—

Svazek periodika

45.

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

HR - Chorvatská republika

Počet stran výsledku

1

Strana od-do

232-232

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—