Způsoby simulace termomechanického zpracování a následného vyhodnocování mikrostruktury TRIP oceli

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014130" target="_blank" >RIV/61989100:27360/06:00014130 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Trip steel thermomechanical processing simulation and subsequent microstructure evaluation concepts

Popis výsledku v původním jazyce

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. It can be achieved excellent combination of mechanical properties - high strength (Rmto 1200 MPa) and eminent formability (ductility to 35%) by treatment of steels with TRIP (transformation induced plasticity) effect utilisation. Fundamental of this feature is stabilisation of substantial amount of retained austenite down to the ambienttemperature at thermomechanical processing and its subsequent transformation for strain induced martensite in consequence of applied plastic deformation. Stability of retained austenite against SIMT (Strain Induced Martensitic Transformation) is main factor affecting plastic properties of material. Microstructure of TRIP steels made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite.

Název v anglickém jazyce

Trip steel thermomechanical processing simulation and subsequent microstructure evaluation concepts

Popis výsledku anglicky

High strength steels with good formability are used for weight reduction in automobile industry especially. TRIP steels are one of these groups of high strength steels. It can be achieved excellent combination of mechanical properties - high strength (Rmto 1200 MPa) and eminent formability (ductility to 35%) by treatment of steels with TRIP (transformation induced plasticity) effect utilisation. Fundamental of this feature is stabilisation of substantial amount of retained austenite down to the ambienttemperature at thermomechanical processing and its subsequent transformation for strain induced martensite in consequence of applied plastic deformation. Stability of retained austenite against SIMT (Strain Induced Martensitic Transformation) is main factor affecting plastic properties of material. Microstructure of TRIP steels made up by multiphase structure of polygonal ferrite, pearlite, bainite, acicular ferrite and certain amount of retained austenite.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0601" target="_blank" >GA106/04/0601: Využití transformačně indukované plasticity (TRIP) u technologií tváření oceli</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

8

Strana od-do

454-461

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—