Výsledná mikrostruktura TRIP oceli s vysokým obsahem hliníku po termomechanickém zpracování

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014139" target="_blank" >RIV/61989100:27360/06:00014139 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Final microstructures of the aluminium bearing TRIP steel detected after thermomechanical processing

Popis výsledku v původním jazyce

There are described experiments containing study of thermomechanical processing parameters effects on the TRIP (= Transformation Induced Plasticity) steel microstructure and specifying optimal thermomechanical processing factors in the report. Aluminiumbearing TRIP-aided steel was used for the performed experiments (0.262 % C, 1.455 % Mn, 1.320 % Al, 0.0204 % Si). Material for specimens was cast, forced to a rod, after that cut and turned into needed size at the end. The simulator Gleeble 1500 was usedfor the simulation of the thermomechanical processing. Final microstructures were evaluated on the bases of transformation curves, optical microscopy foundations and EBSD (= Electron Backscatter Diffraction). The CCT (= Continuous Cooling Transformation) diagram was plotted using dilatometric data. Experiments resulted in detection of higher bainitic contents and lower volume of retained austenite in the specimens cooled with higher cooling rate compared to slower cooled specimens.

Název v anglickém jazyce

Final microstructures of the aluminium bearing TRIP steel detected after thermomechanical processing

Popis výsledku anglicky

There are described experiments containing study of thermomechanical processing parameters effects on the TRIP (= Transformation Induced Plasticity) steel microstructure and specifying optimal thermomechanical processing factors in the report. Aluminiumbearing TRIP-aided steel was used for the performed experiments (0.262 % C, 1.455 % Mn, 1.320 % Al, 0.0204 % Si). Material for specimens was cast, forced to a rod, after that cut and turned into needed size at the end. The simulator Gleeble 1500 was usedfor the simulation of the thermomechanical processing. Final microstructures were evaluated on the bases of transformation curves, optical microscopy foundations and EBSD (= Electron Backscatter Diffraction). The CCT (= Continuous Cooling Transformation) diagram was plotted using dilatometric data. Experiments resulted in detection of higher bainitic contents and lower volume of retained austenite in the specimens cooled with higher cooling rate compared to slower cooled specimens.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0601" target="_blank" >GA106/04/0601: Využití transformačně indukované plasticity (TRIP) u technologií tváření oceli</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

JUNIOR EUROMAT 2006

ISBN

80-214-2984-4

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

1-7

Název nakladatele

Deutsche Gesellschaft für Materielkunde EV

Místo vydání

Frankfurt

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—