Použití akustické emise při měření termomechanických vlastností hořčíkové slitiny AZ61

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014338" target="_blank" >RIV/61989100:27360/06:00014338 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Using acoustic emission in measuring thermomechanical properties of magnesium alloy - AZ61

Popis výsledku v původním jazyce

Knowledge of the relaxation properties of metal materials at high temperatures is necessary for the verification of susceptibility of castings to the creation of defects during the production process. Temperature limits of materials where highest tensionvalues are generated may be detected with tensile tests under high temperatures. The generated tensions in the casting are a cause of the creation and development of defects. At acoustic emission (hereinafter called the "AE") use, tensile tests at hightemperatures may, among other things, be used for analysis of the AE signal sources and set, in more detail, the temperature limit of elastic-plastic deformations existence in the material under examination. The AE is, during tensile tests at high temperatures, based on scanning of released elastic waves generated by sharp tension changes in the body as a result of the subsequent physical-metallurgical processes such as plastic deformation, tension redistributing, creation of microcracks

Název v anglickém jazyce

Using acoustic emission in measuring thermomechanical properties of magnesium alloy - AZ61

Popis výsledku anglicky

Knowledge of the relaxation properties of metal materials at high temperatures is necessary for the verification of susceptibility of castings to the creation of defects during the production process. Temperature limits of materials where highest tensionvalues are generated may be detected with tensile tests under high temperatures. The generated tensions in the casting are a cause of the creation and development of defects. At acoustic emission (hereinafter called the "AE") use, tensile tests at hightemperatures may, among other things, be used for analysis of the AE signal sources and set, in more detail, the temperature limit of elastic-plastic deformations existence in the material under examination. The AE is, during tensile tests at high temperatures, based on scanning of released elastic waves generated by sharp tension changes in the body as a result of the subsequent physical-metallurgical processes such as plastic deformation, tension redistributing, creation of microcracks

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Neue Werkstoffe, neue Technologien und neue energetische Ressourcen fürs 21. Jahrhundert II.

ISBN

80-248-1250-9

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

30-39

Název nakladatele

Ediční středisko VŠB-TU Ostrava

Místo vydání

Ostrava

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—