Grain refinement of Cu and Ni-Ti shape memory alloys by ECAP process

Popis výsledku v původním jazyce

This paper was aimed at verification of functionality of the ECAP technology at extrusion of the copper and Ni-Ti alloys. Cross-section of original samples was 8 x 8 mm and their length was 32 mm. The samples of Cu were extruded at room temperature. Forthe samples of Ni-Ti alloys was used the twostage pressing, when the samples were extruded at temperature of approx. T1 520 degree C and T2 = 420 degree C. In order to increase the concentration of deformation in volume of the sample, the samples were turned around their longitudinal axis by 90 degree after individual passes and they were extruded again. Analysis of structure was made by using of light microscopy

Název v anglickém jazyce

Grain refinement of Cu and Ni-Ti shape memory alloys by ECAP process

Popis výsledku anglicky

This paper was aimed at verification of functionality of the ECAP technology at extrusion of the copper and Ni-Ti alloys. Cross-section of original samples was 8 x 8 mm and their length was 32 mm. The samples of Cu were extruded at room temperature. Forthe samples of Ni-Ti alloys was used the twostage pressing, when the samples were extruded at temperature of approx. T1 520 degree C and T2 = 420 degree C. In order to increase the concentration of deformation in volume of the sample, the samples were turned around their longitudinal axis by 90 degree after individual passes and they were extruded again. Analysis of structure was made by using of light microscopy

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FI-IM%2F033" target="_blank" >FI-IM/033: Výzkum a využití nanotechnologií a výroby nanostrukturních materiálů s vysokými pevnostními vlastnostmi pro moderní konstrukce.</a><br>

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Achievements in Materials and Manufacturing Engineering

ISSN

1734-8412

e-ISSN

—

Svazek periodika

20

Číslo periodika v rámci svazku

1-2

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

5

Strana od-do

247-251

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—