Studium vlivu rychlosti ochlazování na mikrosegregační chování a strukturní heterogenitu superslitiny IN 738LC.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00015295" target="_blank" >RIV/61989100:27360/07:00015295 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Study of cooling rate effect on microsegregation behaviour and structural heterogeneity of IN 738LC superalloy.

Popis výsledku v původním jazyce

The paper deals with the effect of cooling rate on solidification behaviour of IN 738LC nickel based superalloy and on resulting structural and chemical microheterogeneity of this alloy. Samples taken from as-received state were heated with controlled ramp rates (1, 5, 10 and 20°C/min) and immediately after melting they were cooled with the same controlled ramp rate with the help of the laboratory experimental system SETARAM SETSYS 18TM TG/DTA/TMA. Then the microanalysis of minority phases was conductedwith use of X-ray spectroscopy and microstructure of the individual samples was documented by scanning electron microscopy. Chemical microheterogeneity was determined on the basis of measured concentration data of selected elements (Al, Ti, Cr, Co, Ni,Nb, Mo, Ta and W) in representative areas of the individual samples structure.

Název v anglickém jazyce

Study of cooling rate effect on microsegregation behaviour and structural heterogeneity of IN 738LC superalloy.

Popis výsledku anglicky

The paper deals with the effect of cooling rate on solidification behaviour of IN 738LC nickel based superalloy and on resulting structural and chemical microheterogeneity of this alloy. Samples taken from as-received state were heated with controlled ramp rates (1, 5, 10 and 20°C/min) and immediately after melting they were cooled with the same controlled ramp rate with the help of the laboratory experimental system SETARAM SETSYS 18TM TG/DTA/TMA. Then the microanalysis of minority phases was conductedwith use of X-ray spectroscopy and microstructure of the individual samples was documented by scanning electron microscopy. Chemical microheterogeneity was determined on the basis of measured concentration data of selected elements (Al, Ti, Cr, Co, Ni,Nb, Mo, Ta and W) in representative areas of the individual samples structure.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Zeszyty naukowe, Mechanika z.86

ISSN

1429-6055

e-ISSN

—

Svazek periodika

89

Číslo periodika v rámci svazku

321

Stát vydavatele periodika

PL - Polská republika

Počet stran výsledku

6

Strana od-do

233-238

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—