ANALÝZA MIKROSTRUKTURNÍCH CHARAKTERISTIK ZVYŠUJÍCÍ ODOLNOST OCELI URČENÉ PRO KYSELÉ PROSTŘEDÍ K VODÍKOVÉMU ZKŘEHÁVÁNÍ

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00015433" target="_blank" >RIV/61989100:27360/07:00015433 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

THE ANALYSIS OF MICROSTRUCTURE CHARACTERISTICS INCREASING THE RESISTANCE OF SOUR GRADE STEEL TO HYDROGEN EMBRITTLEMENT

Popis výsledku v původním jazyce

Hydrogen induced cracking (HIC) of steel occurs in corrosive environment containing wet hydrogen sulphide what corresponds to the connection of steel exposition in oil and wet sour gas. The physical metallurgy parameters of the pipeline steels governingtheir HIC resistance and response to sour service condition are analysed. The combination of controlled rolling (CR) with accelerated cooling (ACC), modifying the obtained microstructure represents a perspective processing leading to the improvement of HIC resistance. The banded microstructure observed after CR usually is replaced in case of ACC application with the uniform ferrite/bainite and/or acicular ferrite microstructure. The physical metallurgy parameters of the ACC processing leading to the achievement of higher service reliability and durability of pipeline steels are discussed.

Název v anglickém jazyce

THE ANALYSIS OF MICROSTRUCTURE CHARACTERISTICS INCREASING THE RESISTANCE OF SOUR GRADE STEEL TO HYDROGEN EMBRITTLEMENT

Popis výsledku anglicky

Hydrogen induced cracking (HIC) of steel occurs in corrosive environment containing wet hydrogen sulphide what corresponds to the connection of steel exposition in oil and wet sour gas. The physical metallurgy parameters of the pipeline steels governingtheir HIC resistance and response to sour service condition are analysed. The combination of controlled rolling (CR) with accelerated cooling (ACC), modifying the obtained microstructure represents a perspective processing leading to the improvement of HIC resistance. The banded microstructure observed after CR usually is replaced in case of ACC application with the uniform ferrite/bainite and/or acicular ferrite microstructure. The physical metallurgy parameters of the ACC processing leading to the achievement of higher service reliability and durability of pipeline steels are discussed.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FI-IM3%2F159" target="_blank" >FI-IM3/159: Výzkum vlivu metalurgicko-technologických faktorů na vlastnosti vysokopevných plechů jakosti X52 až X70 pro kyselá a nekyselá prostředí.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca

ISSN

1335-1532

e-ISSN

—

Svazek periodika

13

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

6

Strana od-do

449-454

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—