Studium vlivu rychlosti ochlazování na transformační teploty slitiny IN 738LC při tuhnutí
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00015877" target="_blank" >RIV/61989100:27360/07:00015877 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study of cooling rate effect on transformation temperatures in the course of IN 738LC solidification
Popis výsledku v původním jazyce
The paper deals with the effect of cooling rate on the values of transformation temperatures of IN 738LC nickel based superalloy. Particular attention was given to the determination of phase transformation temperatures in the course of solidification andcooling and to the effect of varying cooling rate on these temperatures. Samples taken from as-received state of superalloy were heated with controlled ramp rates (1, 5, 10 and 20°C/min) and immediately after melting they were cooled with the same controlled ramp rate with the help of the laboratory experimental system SETARAM SETSYS 18TM TG/DTA/TMA. The technique of Differential Thermal Analysis (DTA) was selected for the detailed study of nickel based superalloys. Then the microanalysis of minority phases was conducted with use of X-ray spectroscopy and microstructure of the individual samples was documented by scanning electron microscopy.
Název v anglickém jazyce
Study of cooling rate effect on transformation temperatures in the course of IN 738LC solidification
Popis výsledku anglicky
The paper deals with the effect of cooling rate on the values of transformation temperatures of IN 738LC nickel based superalloy. Particular attention was given to the determination of phase transformation temperatures in the course of solidification andcooling and to the effect of varying cooling rate on these temperatures. Samples taken from as-received state of superalloy were heated with controlled ramp rates (1, 5, 10 and 20°C/min) and immediately after melting they were cooled with the same controlled ramp rate with the help of the laboratory experimental system SETARAM SETSYS 18TM TG/DTA/TMA. The technique of Differential Thermal Analysis (DTA) was selected for the detailed study of nickel based superalloys. Then the microanalysis of minority phases was conducted with use of X-ray spectroscopy and microstructure of the individual samples was documented by scanning electron microscopy.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca
ISSN
1335-1532
e-ISSN
—
Svazek periodika
13
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
6
Strana od-do
539-545
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—